ASA+PA Romiloy® 3020/01-4 M10 ROMIRA GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | ROMIRA GERMANY/Romiloy® 3020/01-4 M10 | |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23到55°C | cm/cm/°C | 1.1E-04 -- |
| Shrinkage rate | 23°C | % | 0.50to0.80 -- |
| Flexural modulus | 23°C | MPa | 2400 1500 |
| Charpy Notched Impact Strength | -30°C | kJ/m² | 5.0 -- |
| Tensile strain | 断裂,50°C | % | >30 -- |
| Tensile modulus | 23°C | MPa | 2950 1700 |
| bending strength | 23°C | MPa | 76.0 57.0 |
| vicat | °C | 123 -- | |
| Impact strength of simply supported beam without notch | 23°C | 无断裂 | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 105 -- |
| Charpy Notched Impact Strength | 23°C | kJ/m² | 7.5 8.5 |
| tensile strength | 23°C | MPa | 52.0 37.0 |
| melt mass-flow rate | 260°C/5.0kg | g/10min | 32 -- |
| Water absorption rate | 23°C,24hr | % | 1.0 -- |
| density | 23°C | g/cm³ | 1.16 -- |
| Impact strength of simply supported beam without notch | -30°C | 无断裂 -- |