Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS C2950 SABIC INNOVATIVE US
CYCOLAC™
Electrical field、Electronic field、Household appliances、Household appliances、Automotive sector
Flame retardant、High mobility、High impact resistance、High temperature resistan、heat-resisting
SGS
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/C2950 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 160 J/m |
| 23°C | ASTM D256 | 530 J/m | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 61.0 J |
| -30°C,TotalEnergy | ASTM D3763 | 54.2 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/C2950 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 123 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/C2950 |
|---|---|---|---|
| Flexural modulus | 100mmSpan | ASTM D790 | 2650 Mpa |
| bending strength | Yield,100mmSpan | ASTM D790 | 102 Mpa |
| elongation | 断裂 | ASTM D638 | 40 % |
| tensile strength | 屈服 | ASTM D638 | 62.7 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/C2950 |
|---|---|---|---|
| Dissipation Factor | 50Hz | ASTM D150 | 5E-03 |
| 60Hz | ASTM D150 | 5E-03 | |
| dielectric constant | 60Hz | ASTM D150 | 3.00 |
| Volume resistivity | ASTM D257 | 1E+17 ohms·cm | |
| dielectric constant | 50Hz | ASTM D150 | 3.00 |
| Dissipation Factor | 100Hz | ASTM D150 | 4.9E-03 |
| Surface Resistivity | ASTM D257 | >1.0E+16 ohms | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| dielectric constant | 100Hz | ASTM D150 | 3.00 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| dielectric strength | 3.20mm,inOil | ASTM D149 | 19 KV/mm |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 1 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/C2950 |
|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL 94 | 5VB |
| 1.5mm | UL 94 | V-0 | |
| Limiting Oxygen Index | ASTM D2863 | 32 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/C2950 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.60 % |
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 10 g/10min |
| Water absorption rate | 24hr | ASTM D570 | 0.10 % |
| 平衡,23°C | ASTM D570 | 0.40 % | |
| density | --2 | ASTM D792 | 1.22 g/cm³ |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.40-0.60 % |
| density | -- | ASTM D792 | 1.18 g/cm³ |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/C2950 |
|---|---|---|---|
| TD：-30to30°C | ASTM D696 | 7.2E-05 cm/cm/°C | |
| Hot deformation temperature (HDT) | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 104 °C |
| thermal conductivity | ASTMC177 | 0.20 W/m/K | |
| Hot deformation temperature (HDT) | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 90.6 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 95.0 °C | |
| vicat | ASTM D15255 | 113 °C | |
| RTI Imp | UL 746 | 85.0 °C | |
| RTI Str | UL 746 | 85.0 °C | |
| MD：-30到30°C | ASTM D696 | 7.2E-05 cm/cm/°C | |
| RTI Elec | UL 746 | 85.0 °C |