PC LUX9230T SABIC INNOVATIVE NANSHA
LEXAN™
Lighting applications
high definition
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX9230T |
|---|---|---|---|
| 23°C | ISO 180/1A | 10 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 79.1 J |
| 23°C | ASTM D256 | 800 J/m |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX9230T |
|---|---|---|---|
| RTI Elec | UL 746 | 130 °C | |
| Horizontal: -40 to 40 ° C | 横向, -40到40℃ | ASTME831 | 7.4E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 127 °C | |
| 0.45MPa, Unanealed, 3.20mm | ASTM D648 | 138 °C | |
| Flow: 23 to 80 ° C | 23到80℃ | ISO 11359-2 | 7E-05 cm/cm/°C |
| RTI Imp | UL 746 | 120 °C | |
| 1.8MPa, Unanealed, 100mm span | ISO 75-2/Ae | 124 °C | |
| Horizontal: 23 to 80 ° C | 横向, 23到80℃ | ISO 11359-2 | 7E-05 cm/cm/°C |
| RTI | UL 746 | 130 °C | |
| Flow: -40 to 40 ° C | ASTME831 | 6.8E-05 cm/cm/°C |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX9230T |
|---|---|---|---|
| yield | ASTM D638 | 62.1 Mpa | |
| ASTM D638 | 6.0 % | ||
| Yield, 50.0mm span | ASTM D790 | 101 Mpa | |
| yield | ISO 527-2/50 | 63.0 Mpa | |
| fracture | ISO 527-2/50 | 60.0 Mpa | |
| ASTM D638 | 67.6 Mpa | ||
| ISO 527-2/50 | 85 % | ||
| ASTM D638 | 130 % | ||
| yield | ISO 527-2/50 | 6.0 % | |
| --8 | ISO 178 | 90.0 Mpa | |
| 50.0mm span | ASTM D790 | 2150 Mpa | |
| --1 | ASTM D638 | 2280 Mpa | |
| --7 | ISO 178 | 2300 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX9230T |
|---|---|---|---|
| Dissipation Factor | 50Hz | ASTM D150 | 1E-03 |
| 60Hz | ASTM D150 | 1E-03 | |
| dielectric constant | 60Hz | ASTM D150 | 2.70 |
| 50Hz | ASTM D150 | 2.70 | |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | ASTM D150 | 0.010 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| dielectric constant | 1MHz | ASTM D150 | 2.70 |
| volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| dielectric strength | 3.20mm,inOil | ASTM D149 | 17 KV/mm |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| arc resistance | ASTM D495 | PLC7 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX9230T |
|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 13.0 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.35 % |
| 平衡,23°C,50%RH | ISO 62 | 0.15 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 14 g/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.60-0.80 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX9230T |
|---|---|---|---|
| UL flame retardant rating | 0.800mm | UL 94 | V-2 |
| Hot filament ignition temperature | 1.00mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 3.05mm | UL 94 | V-0 |
| Burning wire flammability index | 1.00mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ISO 4589-2 | 35 % |