PA612 IF006 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Plastic bag
Thermal stability,High lubrication
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/IF006 |
---|---|---|---|
Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTM D648 | 198 °C |
0.45MPa,Unannealed,3.20mm | ASTM D648 | 214 °C | |
Linear coefficient of thermal expansion | MD:-40to40°C | ASTME831 | 4.1E-05 cm/cm/°C |
TD:-40to40°C | ISO 11359-2 | 7.3E-05 cm/cm/°C | |
TD:-40to40°C | ASTME831 | 7.3E-05 cm/cm/°C | |
MD:-40to40°C | ISO 11359-2 | 4.1E-05 cm/cm/°C |
mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/IF006 |
---|---|---|---|
Bending modulus | ISO 178 | 8830 Mpa | |
ASTM D790 | 9310 Mpa | ||
bending strength | ASTM D790 | 291 Mpa | |
ISO 178 | 250 Mpa | ||
elongation | Break | ASTM D638 | 3.7 % |
Tensile modulus | ISO 527-2/1 | 10300 Mpa | |
ASTM D638 | 9580 Mpa | ||
Tensile strain | Break | ISO 527-2 | 3.4 % |
tensile strength | Break | ASTM D638 | 182 Mpa |
Break | ISO 527-2 | 178 Mpa |
Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/IF006 |
---|---|---|---|
Shrinkage rate | TD:24hr | ASTM D955 | 0.70-0.80 % |
TD:24hr | ISO 294-4 | 0.66-0.71 % | |
MD:24hr | ISO 294-4 | 0.11-0.16 % | |
MD:24hr | ASTM D955 | 0.10-0.20 % | |
Water absorption rate | 24hr,50%RH | ASTM D570 | 0.18 % |
impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/IF006 |
---|---|---|---|
Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 14.0 J |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 14 kJ/m² |
Multi axis Instrumented Impact Energy | ISO 6603-2 | 3.04 J | |
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 78 kJ/m² |
flammability | Test Condition | Test Method | SABIC INNOVATIVE US/IF006 |
---|---|---|---|
UL flame retardant rating | 1.5mm | UL 94 | HB |