Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI EC008PXQ SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and Electrical
Thermal stability、Low temperature resistanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/EC008PXQ |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 34 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 7.30 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.9 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/EC008PXQ |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 112 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/EC008PXQ |
|---|---|---|---|
| Poisson's ratio | ASTM D638 | 0.40 | |
| Tensile modulus | ISO 527-2/1 | 35500 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 247 Mpa |
| shear strength | ASTMC273 | 120 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 272 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 32600 Mpa |
| shear modulus | ASTMC273 | 4660 Mpa | |
| Tensile modulus | ASTM D638 | 38600 Mpa | |
| elongation | 断裂 | ASTM D638 | 1.0 % |
| bending strength | ISO 178 | 364 Mpa | |
| compressive strength | 内部方法 | 222 Mpa | |
| Flexural modulus | ISO 178 | 30600 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 0.90 % |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 372 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/EC008PXQ |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 4.5E+02 ohms·cm | |
| Surface Resistivity | ASTM D257 | 4.1E+03 ohms |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/EC008PXQ |
|---|---|---|---|
| Shrinkage rate | MD：24小时 | ASTM D955 | 0.010-0.050 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.11 % |
| melt mass-flow rate | 380°C/6.7kg | ASTM D1238 | 15 g/10min |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.10-0.50 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/EC008PXQ |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-40to150°C | ASTME831 | 2.7E-06 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 193 °C |
| Linear coefficient of thermal expansion | TD：-40to150°C | ASTME831 | 3.6E-05 cm/cm/°C |