PBT 2000 JAPAN POLYPLASTIC
DURANEX®
Casters,Fitness equipment
Glass fiber reinforced,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/2000 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 90 |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/2000 |
|---|---|---|---|
| ColorNumber | EF2001/PLT9908 |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/2000 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 89 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D179/1eA | 3.2 kJ/m² | |
| Flexural modulus | ASTM D790/ISO 178 | 2500 kg/cm²(MPa)[Lb/in²] | |
| ASTM D178 | 2500 Mpa | ||
| elongation at break | ASTM D638/ISO 527 | 20 % | |
| tensile strength | ASTM D638/ISO 527 | 60 kg/cm²(MPa)[Lb/in²] | |
| Tensile strain | 断裂 | ASTM D527-1 | 20 % |
| tensile strength | ISO 527-2 | 60.0 Mpa | |
| bending strength | ASTM D178 | 89 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 20 % | |
| bending strength | ISO 178 | 89.0 Mpa | |
| tensile strength | ASTM D527-1 | 60 Mpa | |
| Flexural modulus | ISO 178 | 2500 Mpa | |
| Heat distortion temperature | 1.8Mpa，HDT | ASTM D75-1 | 73 °C |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/2000 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 5E+16 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 17 KV/mm |
| Volume resistivity | ASTM D257/IEC 60093 | 5.0 x 10^16 Ω.cm | |
| IEC 60093 | 5×1016 Ω.cm | ||
| Surface Resistivity | IEC 60093 | 7×1016 Ω |
| Physical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/2000 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.31 |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/2000 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/2000 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/2000 |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTM D11359 | 10 ×10-5/℃ | |
| Combustibility (rate) | UL 94 | HB | |
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 1.1E-04 cm/cm/°C |
| MD：23到55°C | 内部方法 | 1.1E-04 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 73.0 °C |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 10 mm/mm.℃ | |
| UL flame retardant rating | UL 94 | HB |