Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 73G30HSL BK416 DUPONT SHENZHEN
Zytel®
Electronic and electrical、Automotive Applications
Thermal stability、Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT SHENZHEN/73G30HSL BK416 |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | 23°C | ISO6603-2 | 3.50 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 16 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 10 kJ/m² |
| 23°C | ISO180/1A | 15 kJ/m² | |
| 23°C | ISO180/1U | 80 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 100 kJ/m² |
| -30°C | ISO179/1eU | 80 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT SHENZHEN/73G30HSL BK416 |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 8.50 µgC/g | |
| Odor | VDA270 | 3.50 |
| hardness | Test Condition | Test Method | DUPONT SHENZHEN/73G30HSL BK416 |
|---|---|---|---|
| H961/30 | ISO2039-1 | 230 Mpa | |
| Rockwell hardness | R级 | ISO2039-2 | 121 |
| Mechanical properties | Test Condition | Test Method | DUPONT SHENZHEN/73G30HSL BK416 |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2 | 190 Mpa |
| TensileCreepModule | 1hr | ISO899-1 | -- Mpa |
| Bending modulus 2 | ISO178 | 8500 Mpa | |
| Bending stress 2 | ISO178 | 280 Mpa | |
| Tensile modulus | ISO527-2 | 9500 Mpa | |
| Tensile creep modulus | 1000hr | ISO899-1 | -- Mpa |
| Tensile strain | 断裂 | ISO527-2 | 3.5 % |
| flammability | Test Condition | Test Method | DUPONT SHENZHEN/73G30HSL BK416 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB |
| 1.5mm | UL94 | HB | |
| atomization | F-value(refraction) | ISO6452 | 95 % |
| Burning rate 4 | 1.00mm | ISO3795 | 50 mm/min |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 0.75mm | IEC60695-11-10,-20 | HB |
| Extreme Oxygen Index 5 | ISO4589-2 | 21 % | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB |
| atomization | G-value(condensate) | ISO6452 | 1E-04 g |
| physical property | Test Condition | Test Method | DUPONT SHENZHEN/73G30HSL BK416 |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.60 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 6.3 % |
| MediumDensity | 1.20 g/cm³ | ||
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 15.0 cm3/10min |
| Shrinkage rate | MD | ISO294-4 | 0.20 % |
| density | ISO1183 | 1.36 g/cm³ | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 1.9 % |
| SpecificHeatCapacity of Melt | 2280 J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 W/m/K |
| Thermal performance | Test Condition | Test Method | DUPONT SHENZHEN/73G30HSL BK416 |
|---|---|---|---|
| TD | ISO11359-2 | 7.5E-05 cm/cm/°C | |
| EffectiveThermal Diffusivity | 9.1E-08 m²/s | ||
| 0.45MPa,未退火 | ISO75-2/B | 220 °C | |
| vicat | ISO306/B50 | 215 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 210 °C | |
| MD | ISO11359-2 | 2.6E-05 cm/cm/°C | |
| Glass transition temperature 3 | ISO11357-2 | 60.0 °C | |
| Melting temperature 5 | ISO11357-3 | 221 °C |