Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 909 ASCEND USA
Vydyne®
--
--
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASCEND USA/909 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| -30°C | ISO 179/1eU | 35 kJ/m² |
| Mechanical properties | Test Condition | Test Method | ASCEND USA/909 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.2 % |
| bending strength | 23°C | ISO 178 | 193 Mpa |
| Flexural modulus | 23°C | ISO 178 | 8300 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 9100 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 132 Mpa |
| Poisson's ratio | ISO 527-2 | 0.40 |
| Electrical performance | Test Condition | Test Method | ASCEND USA/909 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | 3.00mm | UL 746 | PLC 3 |
| arc resistance | 3.00mm | ASTM D495 | PLC6 |
| Hot wire ignition (HWI) | 0.75mm | UL 746 | PLC 0 |
| 1.5mm | UL 746 | PLC 0 | |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 0 |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | V |
| High arc combustion index (HAI) | 0.75mm | UL 746 | PLC 0 |
| other | Test Condition | Test Method | ASCEND USA/909 |
|---|---|---|---|
| notes | 加纤30%.防火V-0.本色。 |
| flammability | Test Condition | Test Method | ASCEND USA/909 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| Burning wire flammability index | 0.40mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 800 °C |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 0.40mm | UL 94 | V-0 |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| 1.5mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 750 °C |
| 0.40mm | IEC 60695-2-13 | 930 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Limiting Oxygen Index | ISO 4589-2 | 32 % | |
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 750 °C |
| physical property | Test Condition | Test Method | ASCEND USA/909 |
|---|---|---|---|
| Shrinkage rate | MD:23°C,2.00mm | ISO 294-4 | 0.40 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.70 % |
| 平衡,23°C,50%RH | ISO 62 | 1.3 % | |
| Shrinkage rate | TD:23°C,2.00mm | ISO 294-4 | 1.0 % |
| Thermal performance | Test Condition | Test Method | ASCEND USA/909 |
|---|---|---|---|
| RTI Str | 0.75mm | UL 746 | 110 °C |
| RTI Imp | 1.5mm | UL 746 | 95.0 °C |
| RTI Elec | 0.40mm | UL 746 | 65.0 °C |
| 3.0mm | UL 746 | 130 °C | |
| RTI Imp | 3.0mm | UL 746 | 95.0 °C |
| RTI Elec | 0.75mm | UL 746 | 130 °C |
| melting temperature | ISO 11357-3 | 250 °C | |
| RTI Imp | 0.40mm | UL 746 | 65.0 °C |
| 0.75mm | UL 746 | 65.0 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 250 °C |
| Linear coefficient of thermal expansion | TD：23to55°C,2.00mm | ISO 11359-2 | 1E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 230 °C |
| RTI Str | 1.5mm | UL 746 | 110 °C |
| 3.0mm | UL 746 | 110 °C | |
| Linear coefficient of thermal expansion | MD：23to55°C,2.00mm | ISO 11359-2 | 2E-05 cm/cm/°C |
| RTI Elec | 1.5mm | UL 746 | 130 °C |
| RTI Str | 0.40mm | UL 746 | 65.0 °C |