PA6 SCANAMID 6 B12^ F30 AS POLYKEMI SWEDEN
--
--
Filler, glass fiber reinforced material, 30%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 6 B12^ F30 AS |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | 无断裂 -- | |
| -20°C | 无断裂 -- | ||
| Charpy Notched Impact Strength | -20°C | kJ/m² | 9.0 -- |
| 23°C | kJ/m² | 14 16 |
| Mechanical properties | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 6 B12^ F30 AS |
|---|---|---|---|
| bending strength | MPa | 190 -- | |
| Flexural modulus | 23°C | MPa | 7100 -- |
| tensile strength | MPa | 127 -- | |
| Tensile strain | 屈服 | % | 9.5 -- |
| 断裂 | % | 10 -- |
| flammability | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 6 B12^ F30 AS |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | HB -- | |
| Hot filament ignition temperature | 2.0mm | °C | 650 -- |
| physical property | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 6 B12^ F30 AS |
|---|---|---|---|
| Shrinkage rate | MD | % | 0.30 -- |
| density | g/cm³ | 1.37 -- | |
| Shrinkage rate | TD | % | 0.90 -- |
| Thermal performance | Test Condition | Test Method | POLYKEMI SWEDEN/SCANAMID 6 B12^ F30 AS |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 213 -- |
| 1.8MPa,未退火，HDT | °C | 198 -- |