Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM TF-20 CF2001 DAICEL MALAYSIA
DURACON®
Fitness equipment,Automotive Applications
wear resistant,High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | DAICEL MALAYSIA/TF-20 CF2001 |
|---|---|---|---|
| ColorNumber | CF2001 |
| Mechanical properties | Test Condition | Test Method | DAICEL MALAYSIA/TF-20 CF2001 |
|---|---|---|---|
| Wear factor | 0.060MPa,0.15m/sec7 | JISK7218 | 200 10^-8mm³/N·m |
| 0.060MPa,0.15m/sec6 | JISK7218 | 200 10^-8mm³/N·m | |
| Tensile modulus | ISO 527-2 | 1700 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 50 % | |
| coefficient of friction | 与钢-动态3 | JISK7218 | 0.30 |
| Wear factor | 0.49MPa,0.30m/sec4 | JISK7218 | <1.0 10^-8mm³/N·m |
| 0.49MPa,0.30m/sec5 | JISK7218 | 100 10^-8mm³/N·m | |
| bending strength | ISO 178 | 57.0 Mpa | |
| Flexural modulus | ISO 178 | 1550 Mpa | |
| coefficient of friction | Dynamic2 | JISK7218 | 0.65 |
| tensile strength | ISO 527-2 | 45.0 Mpa |
| Electrical performance | Test Condition | Test Method | DAICEL MALAYSIA/TF-20 CF2001 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 2E+13 ohms·cm | |
| Surface Resistivity | IEC 60093 | 8E+13 ohms |
| physical property | Test Condition | Test Method | DAICEL MALAYSIA/TF-20 CF2001 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 7.00 cm3/10min |
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 1.8 % |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 8.0 g/10min |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 1.6 % |
| Thermal performance | Test Condition | Test Method | DAICEL MALAYSIA/TF-20 CF2001 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 1.3E-04 cm/cm/°C |
| MD：23到55°C | 内部方法 | 1.2E-04 cm/cm/°C |