Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO(PPE)+PS+PA NORYL GTX™ GTX987 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/NORYL GTX™ GTX987 resin |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 kJ/m² |
| Impact strength of cantilever beam gap | -30°C8 | ISO 180/1A | 8.0 kJ/m² |
| -30°C | ASTM D256 | 70 J/m | |
| 23°C | ASTM D256 | 90 J/m | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 10.0 J |
| Impact strength of cantilever beam gap | 23°C8 | ISO 180/1A | 15 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC/NORYL GTX™ GTX987 resin |
|---|---|---|---|
| tensile strength | 屈服3 | ASTM D638 | 55.0 MPa |
| elongation | 断裂3 | ASTM D638 | 15 % |
| 断裂 | ISO 527-2/50 | 20 % | |
| Flexural modulus | --5 | ISO 178 | 2800 MPa |
| Tensile modulus | -- | ISO 527-2/1 | 3000 MPa |
| bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 95.0 MPa |
| tensile strength | 屈服 | ISO 527-2/50 | 62.0 MPa |
| Flexural modulus | 50.0mm跨距4 | ASTM D790 | 2700 MPa |
| bending strength | --5,6 | ISO 178 | 90.0 MPa |
| elongation | 屈服 | ISO 527-2/50 | 5.0 % |
| 屈服3 | ASTM D638 | 5.0 % | |
| tensile strength | 断裂3 | ASTM D638 | 55.0 MPa |
| Tensile modulus | --2 | ASTM D638 | 3250 MPa |
| tensile strength | 断裂 | ISO 527-2/50 | 62.0 MPa |
| physical property | Test Condition | Test Method | SABIC/NORYL GTX™ GTX987 resin |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 1.0to1.4 % |
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 7.50 cm³/10min |
| density | ASTMD792 | 1.25 g/cm³ | |
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 8.5 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.90 % |
| 饱和,23°C | ISO 62 | 3.0 % |
| Thermal performance | Test Condition | Test Method | SABIC/NORYL GTX™ GTX987 resin |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:-40到60°C | ASTME831 | 6E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,64.0mm跨距9，HDT | ISO 75-2/Bf | 190 °C |
| vicat | -- | ISO 306/B120 | 200 °C |
| -- | ASTM D152510 | 192 °C | |
| Linear coefficient of thermal expansion | TD:23到60°C | ISO 11359-2 | 7.5E-05 cm/cm/°C |
| MD:23到60°C | ISO 11359-2 | 7E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 185 °C |
| vicat | -- | ISO 306/B50 | 198 °C |
| Linear coefficient of thermal expansion | MD:-40到60°C | ASTME831 | 5.5E-05 cm/cm/°C |