Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT DR48-BK1762 SABIC INNOVATIVE SHANGHAI
VALOX™
Side track application、Non specific food、Lawn equipment、Garden equipment、Industrial applications、Automotive External Parts、Electrical field、Electronic field、Architectural application、Outdoor applications、Electrical appliances、Engine hood parts、Medical supplies、Nursing supplies、Plastic bag、Automotive interior parts、Casters
Flame retardant、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/DR48-BK1762 |
|---|---|---|---|
| RTI | UL 746 | 140 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 182 °C |
| Coefficient of Linear Thermal Expansion (Flow) | 60 到 138°C | ASTM E831 | 2.0E-5 cm/cm/°C |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 210 °C |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| RTI Imp | UL 746 | 120 °C | |
| RTI Elec | UL 746 | 120 °C | |
| Coefficient of Linear Thermal Expansion (Flow) | -40 到 40°C | ASTM E831 | 2.0E-5 cm/cm/°C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/DR48-BK1762 |
|---|---|---|---|
| Rockwell Hardness | R 级 | ASTM D785 | 118 |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/DR48-BK1762 |
|---|---|---|---|
| Middle Temperature | 245 到 260 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Shot Size | 40 到 80 % | ||
| Drying Temperature | 120 °C | ||
| Mold Temperature | 65 到 90 °C | ||
| Vent Depth | 0.025 到 0.038 mm | ||
| Suggested Max Moisture | 0.020 % | ||
| Processing (Melt) Temp | 250 到 265 °C | ||
| Rear Temperature | 240 到 255 °C | ||
| Nozzle Temperature | 245 到 260 °C | ||
| Front Temperature | 250 到 265 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 50 到 80 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/DR48-BK1762 |
|---|---|---|---|
| Modeling Shrinkage | 流动 : 3.20 到 4.60 mm | 内部方法 | 0.60 到 0.90 % |
| 横向流动 : 1.50 到 3.20 mm | 内部方法 | 0.50 到 0.80 % | |
| Specific Volume | ASTM D792 | 0.650 cm³/g | |
| Moisture Absorption | 24 hr | ASTM D570 | 0.070 % |
| Modeling Shrinkage | 流动 : 1.50 到 3.20 mm | 内部方法 | 0.40 到 0.60 % |
| 横向流动 : 3.20 到 4.60 mm | 内部方法 | 0.80 到 1.1 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/DR48-BK1762 |
|---|---|---|---|
| Flexural Strength | 断裂, 50.0 mm 跨距 | ASTM D790 | 140 Mpa |
| Tensile Strength | 断裂 | ASTM D638 | 93.0 Mpa |
| Flexural Modulus | 50.0 mm 跨距 | ASTM D790 | 5200 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/DR48-BK1762 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 500 J/m |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/DR48-BK1762 |
|---|---|---|---|
| Glow Wire Ignition Temperature | 1.0 mm | IEC 60695-2-13 | 700 °C |
| UL flame retardant rating | 3.0 mm | UL 94 | 5VA |
| Oxygen Index | ASTM D2863 | 29 % | |
| UL flame retardant rating | 0.9 mm | UL 94 | V-0 |
| Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 3.0 mm | IEC 60695-2-13 | 725 °C |
| Glow Wire Flammability Index | 3.0 mm 6 | IEC 60695-2-12 | 960 °C |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/DR48-BK1762 |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | 1.0E+15 ohms·cm | |
| Dielectric Strength | 3.20 mm, in Air | ASTM D149 | 19 KV/mm |
| Hot-wire Ignition | UL 746 | PLC 3 | |
| Dielectric Constant | 1 MHz | ASTM D150 | 3.40 |
| Arc Resistance | ASTM D495 | PLC 6 | |
| Dissipation Factor? | 1 MHz | ASTM D150 | 0.016 |
| Comparative Tracking Index | UL 746 | PLC 3 | |
| High Amp Arc Ignition | UL 746 | PLC 0 | |
| Dielectric Constant | 100 Hz | ASTM D150 | 3.60 |
| Dielectric Strength | 1.60 mm, in Oil | ASTM D149 | 25 KV/mm |
| Dissipation Factor? | 100 Hz | ASTM D150 | 2.0E-3 |
| High Voltage Arc Tracking Rate | UL 746 | PLC 4 |