LCP FIT72 D-2 BK210P CELANESE USA
VECTRA® 
Fitness equipment、Home appliance components、Automotive Applications
Electrostatic discharge p、Halogen-free、Flame retardant、enhance、Glass fiber reinforced、Low warpage, high flowabi、Filler: Glass mineral、35% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodCELANESE USA/FIT72 D-2 BK210P
Impact strength of simply supported beam without notch23°CISO 179/1eU30 kJ/m²
Mechanical propertiesTest ConditionTest MethodCELANESE USA/FIT72 D-2 BK210P
Fracture bending strainISO 1782.5 %
Tensile strain断裂ISO 527-2/1A/502.0 %
Tensile modulusISO 527-2/1A/112000 Mpa
Flexural modulus23℃ISO 17812000 Mpa
tensile strength 断裂ISO 527-2/1A/5110 Mpa
Impact strength of simply supported beam without notch23℃ISO 179/1eA30 kJ/m²
tensile strength 断裂ISO 527-2/1A/50110 Mpa
bending strength23°CISO 178140 Mpa
Flexural modulus23°CISO 17812000 Mpa
Tensile strain断裂ISO 527-2/1A/52 %
Fracture bending strainISO 1782.5 %
bending strength23℃ISO 178140 Mpa
Charpy Notched Impact Strength23℃ISO 179/1eA8 kJ/m²
physical property Test ConditionTest MethodCELANESE USA/FIT72 D-2 BK210P
Shrinkage rateTDISO 294-40.43 %
MDISO 294-40.050 %
Thermal performanceTest ConditionTest MethodCELANESE USA/FIT72 D-2 BK210P
melting temperatureISO 11357-3331 °C
Heat distortion temperature0.45 MPa, 未退火，HDTISO 75-2/B284 °C
0.45MPa,未退火，HDTISO 75-2/B284 °C
Linear coefficient of thermal expansionTDISO 11359-24.3E-05 cm/cm/℃
Heat distortion temperature1.8 MPa, 未退火，HDTISO 75-2/A240 °C
1.8MPa,未退火，HDTISO 75-2/A240 °C
Linear coefficient of thermal expansionMDISO 11359-28E-06 cm/cm/°C
MDISO 11359-28E-06 cm/cm/℃
TDISO 11359-24.3E-05 cm/cm/°C