Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL9112R SABIC INNOVATIVE US
LEXAN™ 
Electronic and Electrical Applications,Plastic bag,lens,Industrial applications
High mobility,Ductility at low temperat,Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodSABIC INNOVATIVE US/EXL9112R
Ball Pressure TestH 358/30ISO 2039-195.0 Mpa
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL9112R
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D648136 °C
1.8 MPa, Unannealed, 3.20 mmASTM D648123 °C
0.45 MPa, Unannealed, 4.00 mm, 100 mm Span10ISO 75-2/Be136 °C
1.8 MPa, Unannealed, 4.00 mm, 100 mm Span10ISO 75-2/Ae124 °C
Linear coefficient of thermal expansionAcross Flow : 23 to 80°CISO 11359-27.5E-5 cm/cm/°C
Flow : -40 to 40°CASTM E8317.2E-5 cm/cm/°C
Across Flow : -40 to 40°CASTM E8317.2E-5 cm/cm/°C
Flow : 23 to 80°CISO 11359-27.5E-5 cm/cm/°C
RTIUL 746130 °C
RTI ElecUL 746130 °C
RTI ImpUL 746120 °C
Vicat softening temperature--ISO 306/B120144 °C
--ASTM D152511143 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL9112R
Bending modulus--5ISO 1782300 Mpa
50.0 mm Span4ASTM D7902330 Mpa
bending strengthYield, 50.0 mm Span4ASTM D79095.0 Mpa
--5,6ISO 17888.0 Mpa
elongationYieldISO 527-2/505.0 %
Yield3ASTM D6385.8 %
Break3ASTM D638100 %
BreakISO 527-2/50100 %
Tensile modulus--2ASTM D6382260 Mpa
--ISO 527-2/12200 Mpa
tensile strengthYieldISO 527-2/5059.0 Mpa
BreakISO 527-2/5055.0 Mpa
Break3ASTM D63858.0 Mpa
Yield3ASTM D63858.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL9112R
Compared to the anti leakage trace indexIEC 60112PLC 3
Dielectric strength3.20 mm, in OilIEC 60243-119 KV/mm
Dissipation factor50 HzIEC 602504.0E-4
60 HzIEC 602504.0E-4
1 MHzIEC 602500.010
Relative permittivity50 HzIEC 602502.70
1 MHzIEC 602502.70
60 HzIEC 602502.70
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL9112R
melt mass-flow rate300°C/1.2 kgASTM D123817 g/10 min
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 113316.0 cm3/10min
Outdoor applicabilityUL 746Cf1
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method0.40 - 0.80 %
Flow : 3.20 mmInternal Method0.40 - 0.80 %
Water absorption rateSaturation, 23°CISO 620.35 %
Equilibrium, 23°C, 50% RHISO 620.15 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL9112R
Charpy Notched Impact Strength23°CISO 179/1eA60 kJ/m²
-30°CISO 179/1eA25 kJ/m²
Dart impact23°C, Total EnergyASTM D376367.0 J
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
23°CISO 180/1U无断裂
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/EXL9112R
Burning wire flammability index1.0 mmIEC 60695-2-12960 °C
Extreme Oxygen IndexISO 4589-240 %
Hot filament ignition temperature1.0 mmIEC 60695-2-13825 °C
UL flame retardant rating3.0 mmUL 945VA
1.5 mmUL 94V-0
injectionTest ConditionTest MethodSABIC INNOVATIVE US/EXL9112R
Back pressure0.300 to 0.700 Mpa
drying temperature120 °C
drying time3.0 to 4.0 hr
Exhaust hole depth0.025 to 0.076 mm
Mold temperature70 to 95 °C
Processing (melt) temperature295 to 315 °C
Screw speed40 to 70 rpm
Spray nozzle temperature290 to 310 °C
Suggested injection volume40 to 60 %
Suggested maximum moisture content0.020 %
Temperature at the front of the material cylinder295 to 315 °C
Temperature at the rear of the barrel215 to 295 °C
Temperature in the middle of the barrel280 to 305 °C