Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 BKV25F30 LANXESS GERMANY
Durethan®
Automotive components、Instrument components、Electronic and Electrical、Industrial applications、Communication equipment
Heat aging
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | LANXESS GERMANY/BKV25F30 |
|---|---|---|---|
| Vicat Softening Temperature | ISO306/B120 | 205 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 215 °C |
| Linear thermal expansion coefficient | TD：23to55°C | ISO11359-2 | 9E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 205 °C |
| Linear thermal expansion coefficient | MD：23到55°C | ISO11359-2 | 2E-05 cm/cm/°C |
| Melting Temperature | ISO11357-3 | 222 °C |
| Additional | Test Condition | Test Method | LANXESS GERMANY/BKV25F30 |
|---|---|---|---|
| ISO Shortname | ISO1874 | PA6,GFHR,14-110,GF25 |
| Physical | Test Condition | Test Method | LANXESS GERMANY/BKV25F30 |
|---|---|---|---|
| Modeling Shrinkage | MD:280°C,2.00mm2 | ISO2577 | 0.30 % |
| MD:120°C,4小时,2.00mm3 | ISO2577 | 0.10 % | |
| TD:280°C,2.00mm2 | ISO2577 | 0.60 % | |
| TD:120°C,4小时,2.00mm3 | ISO2577 | 0.10 % |
| Mechanical Properties | Test Condition | Test Method | LANXESS GERMANY/BKV25F30 |
|---|---|---|---|
| Tensile Strain | 断裂,23°C | ISO527-2/5 | 2.3 % |
| Tensile Modulus | 23°C | ISO527-2/1 | 11000 Mpa |
| Flexural Strain | 23°C | ISO178/A | 2.5 % |
| Tensile Stress | 断裂,23°C | ISO527-2/5 | 150 Mpa |
| Flexural Stress | 23°C | ISO178/A | 230 Mpa |
| Flexural Modulus | 23°C | ISO178/A | 10000 Mpa |
| Impact Properties | Test Condition | Test Method | LANXESS GERMANY/BKV25F30 |
|---|---|---|---|
| Multi-Axial Instrumented Impact Peak Force | 23°C | ISO6603-2 | 1000 N |
| Multi-Axial Instrumented Impact Energy | -30°C | ISO6603-2 | 1.90 J |
| Multi-Axial Instrumented Impact Peak Force | -30°C | ISO6603-2 | 900 N |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 55 kJ/m² |
| Notched Izod impact strength | -30°C | ISO180/1U | 45 kJ/m² |
| 23°C | ISO180/1U | 50 kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 45 kJ/m² |
| Multi-Axial Instrumented Impact Energy | 23°C | ISO6603-2 | 3.00 J |
| Flammability | Test Condition | Test Method | LANXESS GERMANY/BKV25F30 |
|---|---|---|---|
| Glow Wire Ignition Temperature | 0.40mm | IEC60695-2-13 | 850 °C |
| Flame Rating | 0.40mm | UL94 | V-0 |
| Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 850 °C |
| Glow Wire Flammability Index | 0.8mm | IEC60695-2-12 | 960 °C |
| 1.5mm | IEC60695-2-12 | 960 °C | |
| Flame Rating | 3.0mm | UL94 | V-05VA |
| Glow Wire Ignition Temperature | 0.8mm | IEC60695-2-13 | 775 °C |
| Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 960 °C |
| 0.40mm | IEC60695-2-12 | 960 °C | |
| Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 775 °C |
| ISO3795 | passed | ||
| Flame Rating | 1.0mm | UL94 | V-05VA |
| Electrical Properties | Test Condition | Test Method | LANXESS GERMANY/BKV25F30 |
|---|---|---|---|
| Comparative Tracking Index | 解决方案A | IEC60112 | 400 V |
| Volume Resistivity | 23°C | IEC60093 | 3.4E+14 ohms·cm |
| Surface Resistivity | IEC60093 | 4.1E+13 ohms |