POM FB-2025S MITSUBISHI ENGINEERING JAPAN
Iupital™
Automotive sector,Electronic and Electrical Applications
wear resistant,High mobility,Glass addition
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FB-2025S |
|---|---|---|---|
| Dielectric loss | 10，正切 | ASTM D150 | -- |
| Surface Resistivity | ASTM D257 | 1×10 | |
| dielectric strength | ASTM D149 | 20 MV/m | |
| dielectric constant | 10 | ASTM D150 | 33 Pf/m |
| Volume resistivity | ASTM D257 | 1×10 |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FB-2025S |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.2mm | ASTM D256 | 64 J/m |
| Rockwell hardness | ASTM D785 | 83 M | |
| tensile strength | 23℃ | ASTM D638 | 61.8 Mpa |
| bending strength | 23℃ | ASTM D790 | 99 Mpa |
| Flexural modulus | 23℃ | ASTM D790 | 3.58 GPa |
| Stretching length | 23℃ | ASTM D638 | 10 % |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FB-2025S |
|---|---|---|---|
| filler content | 25 % | ||
| Shrinkage rate | 平行方向 | 1.6 % | |
| Water absorption rate | ASTM D570 | 0.20 % | |
| melt mass-flow rate | ASTM D1238 | 5.0 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FB-2025S |
|---|---|---|---|
| Heat distortion temperature | 455Kpa，HDT | ASTM D648 | 162 °C |
| 820Kpa，HDT | ASTM D648 | 135 °C | |
| UL flame retardant rating | UL 94 | HB |