Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 153HSL NC010 DUPONT USA
Zytel®
Home appliance components,Automotive Applications
Thermal stability,High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | DUPONT USA/153HSL NC010 |
|---|---|---|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO 75-2/B | 135 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 62.0 °C | |
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| MD：-- | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| MD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| MD：55to160°C | ISO 11359-2 | 1.7E-04 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1.8E-04 cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO 11359-2 | 7E-08 m²/s | |
| Melting temperature | ISO 11357-3 | 218 °C | |
| Vicat softening temperature | ISO 306/B50 | 180 °C |
| film | Test Condition | Test Method | DUPONT USA/153HSL NC010 |
|---|---|---|---|
| Tensile strain | Yield，MD | ISO 527-3 | 4.4 % |
| mechanical properties | Test Condition | Test Method | DUPONT USA/153HSL NC010 |
|---|---|---|---|
| Bending modulus | ISO 178 | 2100 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 30 % | |
| Tensile modulus | ISO 527-2 | 2400 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 4.4 % |
| tensile strength | 屈服 | ISO 527-2 | 62.0 Mpa |
| Wear resistance | ISO 4649 | 6.00 mm³ |
| Electrical performance | Test Condition | Test Method | DUPONT USA/153HSL NC010 |
|---|---|---|---|
| Compared to the anti leakage trace index | IEC 60112 | PLC 0 | |
| Dielectric strength | IEC 60243-1 | 30 KV/mm | |
| Dissipation factor | 1MHz | IEC 60250 | 0.016 |
| 100Hz | IEC 60250 | 0.014 | |
| Relative permittivity | 100Hz | IEC 60250 | 3.60 |
| 1MHz | IEC 60250 | 3.20 | |
| Surface resistivity | IEC 60093 | -- ohms | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm |
| Physical properties | Test Condition | Test Method | DUPONT USA/153HSL NC010 |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294-4 | 1.3 % |
| TD | ISO 294-4 | 1.4 % | |
| Stickiness | 96%H2SO4 | ISO 307 | 115 cm³/g |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.3 % |
| 饱和,23°C,2.00mm | ISO 62 | 3.0 % |
| impact performance | Test Condition | Test Method | DUPONT USA/153HSL NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| flammability | Test Condition | Test Method | DUPONT USA/153HSL NC010 |
|---|---|---|---|
| Burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| Extreme Oxygen Index | ISO 4589-2 | 27 % | |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 0.9mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | UL 94 | HB | |
| 0.9mm | UL 94 | HB |