PES E2010HC BASF GERMANY
Ultraform®E
medical care、Home appliance components
High temperature resistan、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/E2010HC |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO180 | 7.5 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO180 | 7.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179 | 7.5 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179 | NoBreak |
| Charpy Notched Impact Strength | 23°C | ISO179 | 7.0 kJ/m² |
| hardness | Test Condition | Test Method | BASF GERMANY/E2010HC |
|---|---|---|---|
| ISO2039-1 | 154 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/E2010HC |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC60250 | 0.014 |
| CTI | IEC60112 | 125 V | |
| dielectric constant | 1MHz | IEC60250 | 3.80 |
| Volume resistivity | IEC60093 | >1.0E+13 ohms·cm | |
| dielectric constant | 100Hz | IEC60250 | 3.90 |
| dielectric strength | IEC60243-1 | 37 KV/mm | |
| Dissipation Factor | 100Hz | IEC60250 | 1.7E-03 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/E2010HC |
|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 2650 Mpa |
| Tensile strain | 屈服,23°C | ISO527-2 | 6.9 % |
| Tensile stress | 屈服,23°C | ISO527-2 | 85.0 Mpa |
| flammability | Test Condition | Test Method | BASF GERMANY/E2010HC |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL94 | V-0 |
| 1.6mm | UL94 | V-0 |
| physical property | Test Condition | Test Method | BASF GERMANY/E2010HC |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.86 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.80 % |
| 饱和,23°C | ISO62 | 2.2 % | |
| Shrinkage rate | MD | ISO294-4 | 0.82 % |
| density | ISO1183 | 1.37 g/cm³ | |
| Melt volume flow rate | 360°C/10.0kg | ISO1133 | 70.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/E2010HC |
|---|---|---|---|
| RTI Elec | 1.6mm | UL746 | 180 °C |
| 3.0mm | UL746 | 180 °C | |
| RTI Str | 1.6mm | UL746 | 190 °C |
| MD | 5.2E-05 cm/cm/°C | ||
| 1.8MPa,未退火 | ISO75-2/A | 205 °C | |
| RTI Imp | 1.6mm | UL746 | 180 °C |
| 3.0mm | UL746 | 180 °C | |
| RTI Str | 3.0mm | UL746 | 190 °C |