Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM 500T NC010 DuPont, European Union
Delrin®
Automotive Applications、fibre
High rigidity、wear resistant、Thermal stability、High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DuPont, European Union/500T NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | NoBreak |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 14 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 14 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 330 kJ/m² |
| hardness | Test Condition | Test Method | DuPont, European Union/500T NC010 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO2039-2 | 79 |
| R计秤 | ISO2039-2 | 117 |
| Supplementary Information | Test Condition | Test Method | DuPont, European Union/500T NC010 |
|---|---|---|---|
| Emission | VDA275 | <8.00 mg/kg | |
| SpecificWear | ASTMD1894 | 40.0 10^-6mm³/N·m | |
| Emissions of Organic Compounds | VDA277 | 3.40 µgC/g |
| Mechanical properties | Test Condition | Test Method | DuPont, European Union/500T NC010 |
|---|---|---|---|
| Bending stress | 3.5%应变 | ISO178 | 60.0 Mpa |
| Nominal tensile fracture strain | ISO527-2 | 35 % | |
| TensileCreepModule | 1hr | ISO899-1 | 2300 Mpa |
| Tensile stress | 屈服 | ISO527-2 | 56.0 Mpa |
| Coefficient of Friction | vs.Itself-Dynamic,1hr | ASTMD1894 | 0.22 |
| Tensile strain | 屈服 | ISO527-2 | 18 % |
| Tensile modulus | ISO527-2 | 2300 Mpa | |
| Flexural modulus | ISO178 | 2100 Mpa | |
| Tensile creep modulus | 1000hr | ISO899-1 | 1200 Mpa |
| Electrical performance | Test Condition | Test Method | DuPont, European Union/500T NC010 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+15 ohms | |
| Relative Permittivity | 100Hz | IEC60250 | 3.60 |
| CTI | IEC60112 | 600 V | |
| Volume resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Relative Permittivity | 1MHz | IEC60250 | 3.60 |
| flammability | Test Condition | Test Method | DuPont, European Union/500T NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB |
| 1.5mm | UL94 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| Burning rate 3 | 1.00mm | ISO3795 | 45 mm/min |
| UL flame retardant rating | 0.75mm | IEC60695-11-10,-20 | HB |
| 1.5mm | IEC60695-11-10,-20 | HB | |
| Fogging-G-value | condensate | ISO6452 | 2E-04 g |
| physical property | Test Condition | Test Method | DuPont, European Union/500T NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.6 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 0.82 % |
| MediumDensity | 1.18 g/cm³ | ||
| melt mass-flow rate | ISO1133 | 12 g/10min | |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 10.0 cm3/10min |
| Shrinkage rate | MD | ISO294-4 | 1.7 % |
| density | ISO1183 | 1.38 g/cm³ | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.21 % |
| Thermal performance | Test Condition | Test Method | DuPont, European Union/500T NC010 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 146 °C |
| AnnealingTemperature | 160 °C | ||
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 78.0 °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1.3E-04 cm/cm/°C |
| vicat | -- | ISO306/A50 | 172 °C |
| melting temperature | ISO11357-3 | 178 °C | |
| AnnealingTime-Optional | 30.0 min/mm | ||
| vicat | -- | ISO306/B50 | 140 °C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 1.2E-04 cm/cm/°C |