Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM VW-09 JAPAN POLYPLASTIC
DURACON®
Fitness equipment,Automotive Applications
wear resistant,High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/VW-09 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 75 |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/VW-09 |
|---|---|---|---|
| ColorNumber | CF2001 |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/VW-09 |
|---|---|---|---|
| Wear factor | 0.98MPa,0.30m/sec4 | JISK7218 | <1.0 10^-8mm³/N·m |
| 0.060MPa,0.15m/sec7 | JISK7218 | 7000 10^-8mm³/N·m | |
| Tensile modulus | ISO 527-2 | 2250 Mpa | |
| Wear factor | 0.98MPa,0.30m/sec5 | JISK7218 | 12 10^-8mm³/N·m |
| 0.060MPa,0.15m/sec6 | JISK7218 | 500 10^-8mm³/N·m | |
| Nominal tensile fracture strain | ISO 527-2 | 45 % | |
| coefficient of friction | 与钢-动态3 | JISK7218 | 0.16 |
| bending strength | ISO 178 | 72.0 Mpa | |
| Flexural modulus | ISO 178 | 2100 Mpa | |
| coefficient of friction | Dynamic2 | JISK7218 | 0.28 |
| tensile strength | ISO 527-2 | 58.0 Mpa |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/VW-09 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/VW-09 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 2.50 cm3/10min |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.60 % |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 3.0 g/10min |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/VW-09 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 1.3E-04 cm/cm/°C |
| MD：23到55°C | 内部方法 | 1.3E-04 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 95.0 °C |