Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 J2500Z HANGZHOU JUHESHUN
--
Mechanical components、switch、Household appliances、Electronic field、Electrical field
antioxidant、High impact resistance、high strength、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | HANGZHOU JUHESHUN/J2500Z |
|---|---|---|---|
| Flexural modulus | 1.3mm/min,23℃ | ASTM D790 | 2048 Mpa |
| tensile strength | 5mm/min,23℃ | ASTM D638 | 66.4 Mpa |
| Tensile modulus | 5mm/min,23℃ | ASTM D638 | 2048 Mpa |
| bending strength | 1.3mm/min,23℃ | ASTM D790 | 100.9 Mpa |
| elongation at break | 5mm/min,23℃ | ASTM D638 | 18.2 % |
| Impact strength of cantilever beam gap | 23℃ | ASTM D256 | 60 J/m |
| Shore hardness | ASTM D2240 | 72 | |
| Impact strength of cantilever beam gap | -30℃,4h | ASTM D256 | 38 J/m |
| Electrical performance | Test Condition | Test Method | HANGZHOU JUHESHUN/J2500Z |
|---|---|---|---|
| Dielectric loss | 1MHZ，正切 | ASTM D150 | 0.03 |
| dielectric constant | 1MHZ | ASTM D150 | 3.30 |
| other | Test Condition | Test Method | HANGZHOU JUHESHUN/J2500Z |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-2 |
| physical property | Test Condition | Test Method | HANGZHOU JUHESHUN/J2500Z |
|---|---|---|---|
| relative viscosity | Q/XJ 7-2011 | 2.55 | |
| Shrinkage rate | 垂直 | ASTM D955 | 0.40 % |
| melt mass-flow rate | 110℃,2h；230℃,2.16kg | ASTM D1238 | 22.9 g/10min |
| Shrinkage rate | 平行 | ASTM D955 | 1.73 % |
| Thermal performance | Test Condition | Test Method | HANGZHOU JUHESHUN/J2500Z |
|---|---|---|---|
| melting temperature | 10℃/min | ASTM E794 | 220 °C |
| Heat distortion temperature | 120℃/h;1.82MPa，HDT | ASTM D648 | 69.2 °C |