PA6 TY A218V35 SOLVAY SHANGHAI
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSOLVAY SHANGHAI/TY A218V35
Impact strength of simply supported beam without notch23°CISO 179/1eU90 kJ/m²
23°CISO 180/1U80 kJ/m²
Mechanical propertiesTest ConditionTest MethodSOLVAY SHANGHAI/TY A218V35
Tensile modulus23°CISO 527-2/1A11400 Mpa
Tensile strain断裂, 23°CISO 527-23.0 %
Tensile stress断裂, 23°CISO 527-2/1A210 Mpa
Flexural modulus23°CISO 1789500 Mpa
23°CASTM D7909800 Mpa
bending strength23°CASTM D790, ISO 178290 Mpa
Electrical performanceTest ConditionTest MethodSOLVAY SHANGHAI/TY A218V35
dielectric strength2.00 mmIEC 60243-134 KV/mm
Dissipation FactorIEC 602500.010
IEC 602503.70
Volume resistivityIEC 600931.0E+15 ohms·cm
CTI解决方案 AIEC 60112400 V
Surface ResistivityIEC 600936.0E+15 ohms
flammabilityTest ConditionTest MethodSOLVAY SHANGHAI/TY A218V35
UL flame retardant rating3.2 mmUL 94HB
0.8 mmUL 94HB
1.6 mmUL 94HB
Limiting Oxygen IndexISO 4589-223 %
physical property Test ConditionTest MethodSOLVAY SHANGHAI/TY A218V35
Water absorption rate平衡, 23°C, 50% RHISO 621.6 %
24 hr, 23°CISO 620.75 %
Shrinkage rate流量ISO 294-40.35 %
Water absorption rate饱和, 23°CISO 625.4 %
Shrinkage rate横向流量ISO 294-41.1 %
Thermal performanceTest ConditionTest MethodSOLVAY SHANGHAI/TY A218V35
melting temperatureISO 11357-3263 °C
Thermal deformation temperature under load1.8 MPa, 未退火ASTM D648, ISO 75-2/Af255 °C
injectionTest ConditionTest MethodSOLVAY SHANGHAI/TY A218V35
Temperature70 到 100 °C
Temperature at the rear of the barrel270 到 280 °C
drying temperature80 °C
Temperature at the front of the material cylinder280 到 290 °C
Suggested maximum moisture content0.20 %
Temperature in the middle of the barrel275 到 285 °C