Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PET XL1339 SABIC INNOVATIVE US
XYLEX™
Automotive components、Electronic and electrical
High heat resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XL1339 |
|---|---|---|---|
| Thermal Conductivity | ASTM C177 | 0.18 W/m/K | |
| Heat Deflection Temperature | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Ae | 105 °C |
| Linear thermal expansion coefficient | 横向 : -30 到 30°C | ASTM D696 | 7.9E-5 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO 306/B50 | 130 °C |
| ISO 306/B120 | 135 °C | ||
| Linear thermal expansion coefficient | 流动 : -30 到 30°C | ASTM D696 | 7.6E-5 cm/cm/°C |
| Heat Deflection Temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Be | 125 °C |
| Vicat Softening Temperature | -- | ISO 306/A50 | 140 °C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/XL1339 |
|---|---|---|---|
| Middle Temperature | 250 到 270 °C | ||
| Drying Time | 4.0 到 6.0 hr | ||
| Suggested Shot Size | 50 到 80 % | ||
| Drying Temperature | 110 °C | ||
| Mold Temperature | 65 到 90 °C | ||
| Vent Depth | 0.013 到 0.020 mm | ||
| Suggested Max Moisture | 0.020 % | ||
| Processing (Melt) Temp | 260 到 275 °C | ||
| Rear Temperature | 245 到 265 °C | ||
| Nozzle Temperature | 255 到 270 °C | ||
| Front Temperature | 255 到 275 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 50 到 80 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/XL1339 |
|---|---|---|---|
| Melt Volume flow Rate | 265°C/1.2 kg | ISO 1133 | 4.00 cm3/10min |
| Modeling Shrinkage | 流动 | 内部方法 | 0.50 到 0.80 % |
| Moisture Absorption | 平衡, 23°C | ASTM D570 | 0.70 % |
| Modeling Shrinkage | 横向流动 | 内部方法 | 0.50 到 0.80 % |
| Moisture Absorption | 24 hr | ASTM D570 | 0.10 % |
| 平衡, 50% RH | 0.20 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XL1339 |
|---|---|---|---|
| Tensile Strength | 断裂 | ISO 527-2/50 | 40.0 Mpa |
| Tensile Elongation | 断裂 3 | ASTM D638 | 110 % |
| Tensile Modulus | 2090 Mpa | ||
| Poisson Ratio | ASTM E132 | 0.40 | |
| Tensile Strength | 屈服 3 | ASTM D638 | 49.0 Mpa |
| Tensile Elongation | 屈服 | ISO 527-2/50 | 5.0 % |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2090 Mpa |
| Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 16.0 mg |
| Tensile Strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| Flexural Stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 94.0 Mpa |
| Tensile Elongation | 屈服 3 | ASTM D638 | 5.0 % |
| Flexural Stress | -- 5, 6 | ISO 178 | 80.0 Mpa |
| Flexural Modulus | -- 5 | 2200 Mpa | |
| Tensile Elongation | 断裂 | ISO 527-2/50 | 70 % |
| Tensile Strength | 断裂 3 | ASTM D638 | 49.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XL1339 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ISO 180/1U | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 35 kJ/m² |
| 23°C | 45 kJ/m² | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | 无断裂 | |
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 |
| Charpy Unnotched Impact Strength | ISO 179/1eU | 无断裂 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XL1339 |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | > 1.0E+14 ohms·cm | |
| Dielectric Constant | 1 MHz | ASTM D150 | 3.10 |
| 60 Hz | 3.30 | ||
| Dissipation Factor? | 1 MHz | 0.020 | |
| Dielectric Constant | 50 kHz | 3.30 | |
| Dielectric Strength | 3.20 mm, in Oil | ASTM D149 | 17 KV/mm |
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms | |
| Dissipation Factor? | 50 Hz | ASTM D150 | 2.0E-3 |
| 60 Hz | 2.0E-3 |