PA12 Grilamid® LV-50H FWA nat EMS-GRIVORY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EMS-GRIVORY/Grilamid® LV-50H FWA nat |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | kJ/m² | 19 20 |
| Impact strength of simply supported beam without notch | 23°C | kJ/m² | 90 80 |
| -30°C | kJ/m² | 90 80 | |
| Charpy Notched Impact Strength | -30°C | kJ/m² | 15 15 |
| hardness | Test Condition | Test Method | EMS-GRIVORY/Grilamid® LV-50H FWA nat |
|---|---|---|---|
| Shore hardness | 邵氏D,15秒 | 82 -- | |
| ball-indentation hardness | MPa | 155 -- |
| Electrical performance | Test Condition | Test Method | EMS-GRIVORY/Grilamid® LV-50H FWA nat |
|---|---|---|---|
| Surface Resistivity | ohms | -- 1E+12 | |
| Compared to the Leakage Tracking Index (CTI) | V | -- | |
| Volume resistivity | ohms·cm | -- 1E+13 | |
| dielectric strength | kV/mm | 35 -- |
| Mechanical properties | Test Condition | Test Method | EMS-GRIVORY/Grilamid® LV-50H FWA nat |
|---|---|---|---|
| Tensile strain | 断裂 | % | 5.0 6.0 |
| Tensile modulus | MPa | 12000 11500 | |
| tensile strength | 断裂 | MPa | 155 135 |
| flammability | Test Condition | Test Method | EMS-GRIVORY/Grilamid® LV-50H FWA nat |
|---|---|---|---|
| Flammability level | 0.8mm | HB -- |
| physical property | Test Condition | Test Method | EMS-GRIVORY/Grilamid® LV-50H FWA nat |
|---|---|---|---|
| Shrinkage rate | MD | % | 0.10 -- |
| density | g/cm³ | 1.47 -- | |
| Water absorption rate | 饱和,23°C | % | 0.80 -- |
| Shrinkage rate | TD | % | 0.50 -- |
| Water absorption rate | 平衡,23°C,50%RH | % | 0.40 -- |
| Thermal performance | Test Condition | Test Method | EMS-GRIVORY/Grilamid® LV-50H FWA nat |
|---|---|---|---|
| Continuous use temperature | --2 | °C | 90.0to120 -- |
| --3 | °C | 150 -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 1.5E-05 -- |
| melting temperature | °C | 178 -- | |
| Heat distortion temperature | 8.0MPa,未退火，HDT | °C | 125 -- |
| 1.8MPa,未退火，HDT | °C | 165 -- | |
| Linear coefficient of thermal expansion | TD | cm/cm/°C | 1.2E-04 -- |