Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PSU GL003 BK（JL-4030 BK） SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and electrical
Hydrolysis resistance、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/GL003 BK（JL-4030 BK） |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 169 °C |
| 0.45MPa,未退火,3.20mm | ASTMD648 | 178 °C | |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 179 °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 170 °C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/GL003 BK（JL-4030 BK） |
|---|---|---|---|
| Moisture Absorption | 24hr,50%RH | ASTMD570 | 0.10 % |
| Modeling Shrinkage | MD：24小时 | ASTMD955 | 0.70to0.90 % |
| TD：24hr | 0.70to0.90 % | ||
| TD:24小时 | ISO294-4 | 0.83 % | |
| MD:24小时 | 0.76 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/GL003 BK（JL-4030 BK） |
|---|---|---|---|
| Flexural Modulus | ISO178 | 2300 Mpa | |
| Coefficient of Friction | Static | ASTMD3702Modified | 0.13 |
| Tensile Elongation | 断裂 | ASTMD638 | 9.9 % |
| Flexural Modulus | ASTMD790 | 2070 Mpa | |
| Flexural Strength | 75.8 Mpa | ||
| Specific Wear Rate | ASTMD3702Modified | 24.5 10^-10in^5-min/ft-lb-hr | |
| Coefficient of Friction | Dynamic | 0.23 | |
| Tensile Strain | 断裂 | ISO527-2 | 12 % |
| Tensile Stress | 55.0 Mpa | ||
| Flexural Stress | ISO178 | 79.0 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 55.2 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/GL003 BK（JL-4030 BK） |
|---|---|---|---|
| 23°C | ISO180/1U | 55 kJ/m² | |
| Notched Izod Impact Strength | ISO180/1A | 6.1 kJ/m² |