Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MVLDPE 5500G STYRON US
DOWLEX™
film
Heat sealing performance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | STYRON US/5500G |
|---|---|---|---|
| Melting temperature (DSC) | 内部方法 | 122 °C | |
| Vicat Softening Temperature | ASTMD1525 | 97.0 °C |
| Films Properties | Test Condition | Test Method | STYRON US/5500G |
|---|---|---|---|
| Film Thickness - Tested) | 25 µm | ||
| Film Puncture Energy | 内部方法 | 5.65 J | |
| Secant Modulus | 1%正割,MD | ASTMD882 | 162 Mpa |
| Tensile Strength | TD:屈服 | ASTMD882 | 10.3 Mpa |
| Tensile Modulus | TD | ASTMD882 | 91.0 J/cm³ |
| Tensile Strength | MD:断裂 | ASTMD882 | 41.4 Mpa |
| Secant Modulus | 1%正割,TD | ASTMD882 | 193 Mpa |
| Tensile Elongation | MD:断裂 | ASTMD882 | 400 % |
| Elmendorf Tear Strength | TD | ASTMD1922 | 600 g |
| Tensile Elongation | TD:断裂 | ASTMD882 | 500 % |
| Film Puncture Force | 内部方法 | 62.3 N | |
| Gardner Impact | ASTMD1709A | 650 g | |
| Secant Modulus | 2%正割,TD | ASTMD882 | 165 Mpa |
| Elmendorf Tear Strength | MD | ASTMD1922 | 350 g |
| Tensile Strength | TD:断裂 | ASTMD882 | 37.9 Mpa |
| Film Puncture Force | 内部方法 | 29.0 J/cm³ | |
| Secant Modulus | 2%正割,MD | ASTMD882 | 141 Mpa |
| Tensile Strength | MD:屈服 | ASTMD882 | 18.3 Mpa |
| Tensile Modulus | MD | ASTMD882 | 82.7 J/cm³ |
| Physical | Test Condition | Test Method | STYRON US/5500G |
|---|---|---|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 1.5 g/10min |
| Optical | Test Condition | Test Method | STYRON US/5500G |
|---|---|---|---|
| Haze | ASTMD1003 | 12 % | |
| Gloss | 45° | ASTMD2457 | 45 |