PBT K4530-1001 SABIC INNOVATIVE US
VALOX™
Plastic bag,Automotive External Parts,Electronic field,Electrical field
Hydrolysis resistance,High mobility,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/K4530-1001 |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy5 | ASTM D3763 | 6.10 J |
| 23°C,TotalEnergy4 | ASTM D3763 | 5.30 J | |
| 23°C,TotalEnergy6 | ASTM D3763 | 4.97 J |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/K4530-1001 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 218 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 193 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/K4530-1001 |
|---|---|---|---|
| flexural modulus | 50.0mm跨距6 | ASTM D790 | 4820 Mpa |
| elongation | 断裂4 | ASTM D638 | 2.3 % |
| flexural modulus | 50.0mm跨距5 | ASTM D790 | 4530 Mpa |
| Tensile modulus | ASTM D638 | 3560 Mpa | |
| elongation | 屈服 | ASTM D638 | 4.0 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 4640 Mpa |
| elongation | 断裂 | ASTM D638 | 4.0 % |
| tensile strength | 屈服 | ASTM D638 | 103 Mpa |
| bending strength | Break,50.0mmSpan | ASTM D790 | 150 Mpa |
| tensile strength | 断裂4 | ASTM D638 | 89.6 Mpa |
| 断裂 | ASTM D638 | 103 Mpa | |
| flexural modulus | 50.0mm跨距4 | ASTM D790 | 5100 Mpa |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/K4530-1001 |
|---|---|---|---|
| shrinkage rate | TD：3.20mm | 内部方法 | 1.0-1.2 % |
| MD：3.20mm | 内部方法 | 0.70-0.90 % |