PC H3000R MITSUBISHI ENGINEERING JAPAN
IUPILON™
Electronic and electrical、Fitness equipment
transparent、standard、High mobility、Good demolding performanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/H3000R |
|---|---|---|---|
| Flexural modulus | 6.40mm | ASTM D790 | 2300 Mpa |
| Dart impact | 3.20mm | ASTM D3029 | 65.0 J |
| elongation | 断裂，3.20mm | ASTM D638 | 100 % |
| bending strength | 6.40mm | ASTM D790 | 87.0 Mpa |
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 250 J/m |
| Rockwell hardness | R计秤 | ASTM D785 | 123 |
| tensile strength | 3.20mm | ASTM D638 | 62.0 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/H3000R |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 2.1E+16 ohm·cm | |
| dielectric constant | ASTM D150 | 2.85 |
| optical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/H3000R |
|---|---|---|---|
| transmissivity | 总计,3000µm | ASTM D1003 | 85.0 % |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/H3000R |
|---|---|---|---|
| Shrinkage rate | MD：3.00mm | ASTM D955 | 0.40-0.80 % |
| Water absorption rate | 24hr | ASTM D570 | 0.24 % |
| melt mass-flow rate | 300℃/1.2kg | ASTM D1238 | 28 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/H3000R |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 128 °C |
| UL flame retardant rating | 1.60mm | UL 94 | V-2 |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 132 °C |
| Linear coefficient of thermal expansion | ASTM D696 | 0.000060-0.000070 cm/cm/℃ |