Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL6013-88225 SABIC EU
LEXAN™
Electronic and Electrical、Aerospace Applications、lens
High mobility、Ductility at low temperat、Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC EU/EXL6013-88225 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 75 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 70 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 60 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 70 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | SABIC EU/EXL6013-88225 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 90.0 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC EU/EXL6013-88225 |
|---|---|---|---|
| relative permittivity | 60Hz | IEC 60250 | 2.70 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| relative permittivity | 50Hz | IEC 60250 | 2.70 |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 2.70 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
| 60Hz | IEC 60250 | 1E-03 | |
| 1MHz | IEC 60250 | 0.010 |
| Mechanical properties | Test Condition | Test Method | SABIC EU/EXL6013-88225 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2100 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| bending strength | ISO 178 | 80.0 Mpa | |
| Flexural modulus | ISO 178 | 2150 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 10.0 mg |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| 屈服 | ISO 527-2/50 | 7.0 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 60.0 Mpa |
| flammability | Test Condition | Test Method | SABIC EU/EXL6013-88225 |
|---|---|---|---|
| UL flame retardant rating | 3.00mm | UL 94 | V-1 |
| Burning wire flammability index | 1.00mm | IEC 60695-2-12 | 850 °C |
| physical property | Test Condition | Test Method | SABIC EU/EXL6013-88225 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 5.50 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.35 % |
| Shrinkage rate | MD1 | 内部方法 | 0.60-0.80 % |
| Thermal performance | Test Condition | Test Method | SABIC EU/EXL6013-88225 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:23到80°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| 0.45MPa, Unanealed, 100mm span | ISO 75-2/Be | 131 °C | |
| Linear coefficient of thermal expansion | MD:23到80°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 100mm span | ISO 75-2/Ae | 122 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
Contact Us
Get App