PA12 SP003 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electrical appliances、Plastic bag
lubrication、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/SP003 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 48 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 7.80 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.6 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 5.00 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/SP003 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 1580 Mpa | |
| elongation | 屈服 | ASTM D638 | 18 % |
| Tensile strain | 屈服 | ISO 527-2 | 18 % |
| tensile strength | 断裂 | ASTM D638 | 35.2 Mpa |
| 断裂 | ISO 527-2 | 36.0 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 13.5 10^-10in^5-min/ft-lb-hr |
| Flexural modulus | ASTM D790 | 1380 Mpa | |
| Tensile modulus | ASTM D638 | 1380 Mpa | |
| elongation | 断裂 | ASTM D638 | 24 % |
| bending strength | ISO 178 | 44.0 Mpa | |
| coefficient of friction | Static | ASTM D3702Modified | 0.14 |
| Tensile strain | 断裂 | ISO 527-2 | 33 % |
| Flexural modulus | ISO 178 | 1300 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 38.0 Mpa |
| 屈服 | ASTM D638 | 37.9 Mpa | |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.23 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/SP003 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 1.0 % |
| MD：24小时 | ASTM D955 | 0.90-1.1 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.20 % |
| Shrinkage rate | TD：24hr | ASTM D955 | 1.8-2.0 % |
| TD:24小时 | ISO 294-4 | 1.9 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/SP003 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 134 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 150 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 147 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 146 °C |