Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DBL-4034 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Plastic bag
Easy to form、Flame retardant、Filler: Glass beads
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DBL-4034 |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 130 °C | |
| 0.45MPa, Unannealed,3.20mm Span | ISO75-2/Bf | 137 °C | |
| Linear thermal expansion coefficient | MD:23到60°C | ISO11359-2 | 6E-05 cm/cm/°C |
| TD:23到60°C | 6.9E-05 cm/cm/°C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DBL-4034 |
|---|---|---|---|
| Flexural Modulus | ISO178 | 2900 Mpa | |
| Tensile Strain | 断裂 | ISO527-2/5 | 4.6 % |
| Specific Wear Rate | ASTMD3702Modified | 94.0 10^-10in^5-min/ft-lb-hr | |
| Flexural Strain (Break) | ISO178 | 5.3 % | |
| Tensile Modulus | ISO527-2/1 | 2800 Mpa | |
| Flexural Stress | ISO178 | 76.0 Mpa | |
| Coefficient of Friction | 与自身-动态 | ASTMD3702Modified | 0.50 |
| Tensile Strain | 屈服 | ISO527-2/5 | 3.1 % |
| Tensile Stress | 断裂 | 40.0 Mpa | |
| 屈服 | 42.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/DBL-4034 |
|---|---|---|---|
| Modeling Shrinkage | MD | 内部方法 | 0.50到0.70 % |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.13 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DBL-4034 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 25 kJ/m² |
| Notched Izod Impact Strength | ISO180/1A | 6.0 kJ/m² |