POM XGC10 CELANESE GERMANY
HOSTAFORM®
Fitness equipment、Automotive Applications、Thin walled products
high strength、filler、Glass fiber reinforced ma、10%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE GERMANY/XGC10 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.5 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CELANESE GERMANY/XGC10 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 4700 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 4200 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 110 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 4.9 % |
| physical property | Test Condition | Test Method | CELANESE GERMANY/XGC10 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 3.00 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.0 % |
| MD | ISO 294-4 | 1.5 % | |
| density | ISO 1183 | 1.48 g/cm³ |
| Thermal performance | Test Condition | Test Method | CELANESE GERMANY/XGC10 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 166 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 154 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6E-05 cm/cm/°C |
| TD | ISO 11359-2 | 8E-05 cm/cm/°C |