PP Copolymer POLYfill PPC T1035 POLYKEMI SWEDEN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYKEMI SWEDEN/POLYfill PPC T1035 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 8.0 kJ/m² |
| -20°C | ISO 179 | 4.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | POLYKEMI SWEDEN/POLYfill PPC T1035 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 2600 MPa |
| tensile strength | ISO 527-2 | 30.0 MPa | |
| Tensile strain | 屈服 | ISO 527-2 | 8.0 % |
| bending strength | ISO 178 | 50.0 MPa |
| flammability | Test Condition | Test Method | POLYKEMI SWEDEN/POLYfill PPC T1035 |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 750 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | POLYKEMI SWEDEN/POLYfill PPC T1035 |
|---|---|---|---|
| density | ISO 1183 | 1.17 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 1.0 g/10min |
| Thermal performance | Test Condition | Test Method | POLYKEMI SWEDEN/POLYfill PPC T1035 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 117 °C |
| vicat | -- | ISO 306/A50 | 144 °C |
| -- | ISO 306/B50 | 60.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 65.0 °C |