PC
PC SABIC INNOVATIVE NANSHA LUX2614-WH4G020X
Light diffusion level
US$ 4,473 / MT
FOB China Main Port
injectionTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX2614-WH4G020X
Back pressure0.300 to 0.700 Mpa
Temperature at the front of the material cylinder310 to 330 °C
Screw speed40 to 70 rpm
Mold temperature80 to 115 °C
Processing (melt) temperature310 to 330 °C
Suggested injection volume40 to 60 %
Suggested maximum moisture content0.020 %
Spray nozzle temperature305 to 325 °C
Exhaust hole depth0.025 to 0.076 mm
drying temperature120 °C
Temperature in the middle of the barrel300 to 320 °C
drying time3.0 to 4.0 hr
Temperature at the rear of the barrel290 to 310 °C
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX2614-WH4G020X
Hot deformation temperature0.45 MPa, Unannealed, 6.40 mmASTM D648137 °C
Linear coefficient of thermal expansion-40 to 95°C，FlowASTM E8316.8E-5 cm/cm/°C
specific heatASTM C3511260 J/kg/°C
Hot deformation temperature1.8 MPa, Unannealed, 6.40 mmASTM D648132 °C
thermal conductivityASTM C1770.29 W/m/K
RTI ElecUL 74680.0 °C
RTI ImpUL 74680.0 °C
RTIUL 74680.0 °C
Vicat softening temperature--ISO 306/B120145 °C
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
Vicat softening temperature--ASTM D15257154 °C
impact performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX2614-WH4G020X
Dart impact23°CASTM D3029169 J
Suspended wall beam without notch impact strength23°CASTM D48123200 J/m
Impact strength of cantilever beam gapASTM D1822546 kJ/m²
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX2614-WH4G020X
Burning wire flammability index0.75 mmIEC 60695-2-12750 °C
Hot filament ignition temperature1.5 mmIEC 60695-2-13850 °C
0.75 mm9IEC 60695-2-13875 °C
UL flame retardant rating0.817mmUL 94V-2
Burning wire flammability index1.5 mmIEC 60695-2-12850 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX2614-WH4G020X
Bending modulus50.0 mm Span3ASTM D7902340 Mpa
bending strengthYield, 50.0 mm Span3ASTM D79093.0 Mpa
--4,5ISO 17894.0 Mpa
elongationYieldISO 527-2/506.0 %
Yield2ASTM D6387.0 %
Tensile modulusISO 527-2/12300 Mpa
Taber abraser1000 Cycles, 1000 g, CS-17 WheelASTM D104410.0 mg
tensile strengthBreakISO 527-2/5063.0 Mpa
elongationBreak2ASTM D638110 %
tensile strengthYield2ASTM D63862.0 Mpa
YieldISO 527-2/5063.0 Mpa
Bending modulus--4ISO 1782300 Mpa
tensile strengthBreak2ASTM D63865.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX2614-WH4G020X
Compared to the anti leakage trace indexUL 746PLC 3
Dissipation factor50 HzASTM D1509.0E-4
60 HzASTM D1509.0E-4
1 MHzASTM D1500.010
Dielectric constant1 MHzASTM D1502.96
Dielectric strength3.20 mm, in AirASTM D14915 KV/mm
High arc combustion indexUL 746PLC 1
Hot wire ignitionUL 746PLC 3
Volume resistivityASTM D257> 1.0E+17 ohms·cm
Dielectric constant60 HzASTM D1503.17
50 kHzASTM D1503.17
hardnessTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX2614-WH4G020X
Rockwell hardnessR-ScaleASTM D785118
M-ScaleASTM D78570
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX2614-WH4G020X
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 11337.00 cm3/10min
Water absorption rate24 hrASTM D5700.15 %
Equilibrium, 100°CASTM D5700.58 %
Specific volumeASTM D7920.830 cm³/g
Outdoor applicabilityUL 746Cf2
Water absorption rateEquilibrium, 23°CASTM D5700.35 %
Shrinkage rate3.20 mm，FlowInternal Method0.50 - 0.70 %
melt mass-flow rate300°C/1.2 kgASTM D12387.0 g/10 min
optical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/LUX2614-WH4G020X
Refractive indexASTM D5421.586

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China