Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 1011CH5KR MITSUBISHI ENGINEERING JAPAN
Novamid®
Electronic and Electrical
Thermal stability、High cycle heat aging
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1011CH5KR |
|---|---|---|---|
| bending strength | D790 | 1030(500) Kgf/cm | |
| Stretching length | D638 | 180(＞200) % | |
| bending strength | D790 | 100(49) Mpa | |
| Impact strength of cantilever beam gap | 1/2寸 | D256 | 59(780) J/m |
| tensile strength | D638 | 800(380) Kgf/cm | |
| Impact strength of cantilever beam gap | 1/2寸 | D256 | 6.0(80) Kgf.cm/cm |
| Flexural modulus | D790 | 2.65(0.98) GPa | |
| Impact strength of cantilever beam gap | 1/8寸 | D256 | 8.2(90) Kgf.cm/cm |
| 1/8寸 | D256 | 80(880) J/m | |
| tensile strength | D638 | 78(37) Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1011CH5KR |
|---|---|---|---|
| Dielectric loss | 正切 | D150 | 0.03(0.1) |
| arc resistance | ℃ | 180-190 S | |
| dielectric strength | D149 | 20(12-15) MV/m | |
| dielectric constant | D150 | 35-44(132) Pf/m |
| processability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1011CH5KR |
|---|---|---|---|
| Shrinkage rate | 0.9/1.5 MD% |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1011CH5KR |
|---|---|---|---|
| Rockwell hardness | D785 | 120(85) R | |
| Water absorption rate | D570 | 3.3 % | |
| Taber wear resistance | D1894 | 7 |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1011CH5KR |
|---|---|---|---|
| Heat distortion temperature | HDT | D648 | 158 °C |
| Linear coefficient of thermal expansion | D696 | 9 | |
| UL flame retardant rating | UL 94 | V-2 |