PLA+PMMA HML5150 Shanghai KumhoSunny Plastics Co., Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./HML5150 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 30 J/m |
| Supplementary Information | Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./HML5150 |
|---|---|---|---|
| CSAFileNo | LS66457 |
| Mechanical properties | Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./HML5150 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 8.0 % |
| tensile strength | ASTM D638 | 70.0 MPa | |
| Flexural modulus | ASTM D790 | 3200 MPa | |
| bending strength | ASTM D790 | 75.0 MPa |
| Electrical performance | Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./HML5150 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| flammability | Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./HML5150 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./HML5150 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.50to0.70 % |
| melt mass-flow rate | 240°C/5.0kg | ASTM D1238 | 6.9 g/10min |
| density | ASTM D792 | 1.21 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 6.9 g/10min |
| Biobased content | 50to60 % |
| Thermal performance | Test Condition | Test Method | Shanghai KumhoSunny Plastics Co., Ltd./HML5150 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 64.5 °C |
| vicat | ASTM D15252 | 67.5 °C |