PC GP-2102 LG CHEM KOREA

LUPOY®

electrical equipment,Lighting applications,Electric,Electronic application field,Phone

High impact resistance,heat-resisting,Good toughness and chemic

Plastic Datasheets

Impact resistance	Test Condition	Test Method	LG CHEM KOREA/GP-2102
Impact strength of cantilever beam gap	23°C, 3.20 mm, 注塑	ASTM D256	270 J/m

hardness	Test Condition	Test Method	LG CHEM KOREA/GP-2102
Rockwell hardness	R 级, 23°C, 注塑	ASTM D785	124

thermal performance	Test Condition	Test Method	LG CHEM KOREA/GP-2102
RTI Elec		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
RTI		UL 746	80.0 °C
Heat Deflection Temperature	1.8 MPa, 未退火, 6.40 mm, 注塑，HDT	ASTM D648	137 °C

Mechanical properties	Test Condition	Test Method	LG CHEM KOREA/GP-2102
flexural modulus	23°C, 3.20 mm, 注塑	ASTM D790	3330 Mpa
bending strength	23°C, 3.20 mm, 注塑	ASTM D790	98.1 Mpa
tensile strength	屈服, 23°C, 3.20 mm, 注塑	ASTM D638	53.9 Mpa
elongation	断裂, 23°C, 3.20 mm, 注塑	ASTM D638	15 %

Physical properties	Test Condition	Test Method	LG CHEM KOREA/GP-2102
shrinkage rate	23°C, 3.20 mm, 注塑，Flow	ASTM D955	0.20 - 0.40 %
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	9.0 g/10 min
density		ASTM D792	1.25 g/cm³

flammability	Test Condition	Test Method	LG CHEM KOREA/GP-2102
UL flame retardant rating	0.75 mm	UL 94	HB

injection	Test Condition	Test Method	LG CHEM KOREA/GP-2102
Minimum Moisture Content			0.020 %
drying time			3.0 to 5.0 hr
screw speed			40 to 70 rpm
Suggested maximum moisture content			0.020 %
Temperature in the middle of the barrel			285 to 300 °C
Temperature at the rear of the barrel			280 to 295 °C
Processing (melt) temperature			295 to 310 °C
mold temperature			90 to 110 °C
drying temperature			100 to 120 °C
Temperature at the front of the material cylinder			290 to 305 °C
Back pressure			0.981 to 3.92 Mpa
Spray nozzle temperature			290 to 305 °C