Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 1809-01 SHANDONG LUXI CHEM
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SHANDONG LUXI CHEM/1809-01 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23℃ | ISO 180 | 66 kJ/m² |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 72 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SHANDONG LUXI CHEM/1809-01 |
|---|---|---|---|
| tensile strength | 断裂50mm/min | ISO 527 | 70 Mpa |
| Tensile modulus | 1mm/min | ISO 527 | 2400 Mpa |
| Tensile strain | 50mm/min | ISO 527 | ＞120 % |
| tensile strength | 屈服50mm/min | ISO 527 | 60 Mpa |
| bending strength | 2mm/min | ISO 178 | 90 Mpa |
| Flexural modulus | 2mm/min | ISO 178 | 2300 Mpa |
| Electrical performance | Test Condition | Test Method | SHANDONG LUXI CHEM/1809-01 |
|---|---|---|---|
| Volume resistivity | 5min | IEC 60093 | 300000000000000000 ohms·cm |
| dielectric constant | IEC 60250 | 2.7 1 MHz | |
| dielectric strength | 1mm | IEC 60243 | 30 KV/mm |
| Dissipation Factor | IEC 60250 | 150 1 MHz |
| optical performance | Test Condition | Test Method | SHANDONG LUXI CHEM/1809-01 |
|---|---|---|---|
| transmittance | 3.2mm | ASTM D1003 | 90 % |
| Haze ratio | 3.2mm | ASTM D1003 | ＜0.5 % |
| Yellowness Index | 380-780nm | ISO 17223 | ＜2 |
| physical property | Test Condition | Test Method | SHANDONG LUXI CHEM/1809-01 |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294 | 0.5-0.7 % |
| melt mass-flow rate | 300℃，1.2kg | ISO 1133 | 9 g/10min |
| Water absorption rate | 23℃，24h | ISO 62 | 0.2 % |
| density | ISO 1183 | 1.2 g/cm³ |
| Thermal performance | Test Condition | Test Method | SHANDONG LUXI CHEM/1809-01 |
|---|---|---|---|
| vicat | B120， 4.0mm | ISO 306 | 148 °C |
| Heat distortion temperature | 1.80MPa，4.0mm，HDT | ISO 75 | 127 °C |
| flammability | 1.5mm | UL 94 | HB |