LLDPE FC18NJ SABIC SAUDI
SABIC®
film、currency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | SABIC SAUDI/FC18NJ |
|---|---|---|---|
| 邵氏D | ISO868 | 55 |
| film | Test Condition | Test Method | SABIC SAUDI/FC18NJ |
|---|---|---|---|
| Falling hammer impact | 30µm | ISO7765-1 | 120 g |
| elongation | MD:断裂,30µm | ISO527-3 | 550 % |
| Film thickness - tested | 30 µm | ||
| Tensile modulus | MD:30µm | ISO527-3 | 190 Mpa |
| Tensile stress | TD:断裂,30µm | ISO527-3 | 40.0 Mpa |
| elongation | TD:断裂,30µm | ISO527-3 | 850 % |
| Tensile modulus | TD:30µm | ISO527-3 | 220 Mpa |
| Tensile stress | MD:断裂,30µm | ISO527-3 | 55.0 Mpa |
| Elmondov tear strength | TD:30µm | ISO6383-2 | 160 N |
| MD:30µm | ISO6383-2 | 30 N |
| Mechanical properties | Test Condition | Test Method | SABIC SAUDI/FC18NJ |
|---|---|---|---|
| Tensile strain | 断裂 | ISO1872-2 | >430 % |
| Tensile stress | 屈服 | ISO1872-2 | 9.00 Mpa |
| Flexural modulus | ISO1872-2 | 200 Mpa |
| optical performance | Test Condition | Test Method | SABIC SAUDI/FC18NJ |
|---|---|---|---|
| Haze ratio | 30.0µm | ISO14782 | 8.0 % |
| physical property | Test Condition | Test Method | SABIC SAUDI/FC18NJ |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ISO1872-2 | 1.0 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC SAUDI/FC18NJ |
|---|---|---|---|
| melting temperature | ISO11357-3 | 122 °C | |
| vicat | ISO306 | 102 °C | |
| brittle temperature | ISO974 | <-70.0 °C |