ASA+PC UMG ALLOY® TA-820CA UMG JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | UMG JAPAN/UMG ALLOY® TA-820CA | |
|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 5.00 cm³/10min |
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| Tensile modulus | 23°C | ISO 527-2 | 9100 MPa |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.5E-05 cm/cm/°C |
| Flexural modulus | 23°C | ISO 178 | 8000 MPa |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| bending strength | 23°C | ISO 178 | 135 MPa |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 6.0 kJ/m² |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 113 °C |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| density | 23°C | ISO 1183 | 1.17 g/cm³ |
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.10to0.30 % |
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 117 |
| tensile strength | 断裂,23°C | ISO 527-2 | 98.0 MPa |