Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 100 TORAY MALAYSIA
Toyolac®
Industrial machinery、Fitness equipment
High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY MALAYSIA/100 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 0°C,3.20mm | ASTM D256 | 230 J/m |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 26 kJ/m² |
| Impact strength of cantilever beam gap | -30°C,12.7mm | ASTM D256 | 140 J/m |
| 23°C,3.20mm | ASTM D256 | 310 J/m | |
| 0°C,12.7mm | ASTM D256 | 200 J/m | |
| 23°C,12.7mm | ASTM D256 | 290 J/m | |
| -30°C,3.20mm | ASTM D256 | 160 J/m |
| hardness | Test Condition | Test Method | TORAY MALAYSIA/100 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 105 |
| Electrical performance | Test Condition | Test Method | TORAY MALAYSIA/100 |
|---|---|---|---|
| Dissipation Factor | 1kHz | ASTM D150 | 6.5E-03 |
| Surface Resistivity | ASTM D257 | >1.0E+16 ohms | |
| dielectric constant | 1kHz | ASTM D150 | 3.10 |
| Volume resistivity | 23°C | ASTM D257 | >1.0E+16 ohms·cm |
| dielectric strength | ASTM D149 | 24 KV/mm |
| Mechanical properties | Test Condition | Test Method | TORAY MALAYSIA/100 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2100 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 44.0 Mpa |
| elongation | 断裂 | ASTM D638 | 40 % |
| bending strength | ISO 178 | 63.0 Mpa | |
| ASTM D790 | 63.0 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 41.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | >10 % |
| Flexural modulus | ASTM D790 | 1960 Mpa |
| flammability | Test Condition | Test Method | TORAY MALAYSIA/100 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY MALAYSIA/100 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40-0.60 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.30 % |
| density | ASTM D792 | 1.04 g/cm³ | |
| ISO 1183 | 1.04 g/cm³ | ||
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | TORAY MALAYSIA/100 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 85.0 °C |
| thermal conductivity | ASTMC177 | 0.15 W/m/K | |
| Heat distortion temperature | 1.8MPa,未退火,12.7mm，HDT | ASTM D648 | 91.0 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 80.0 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 7.6E-05 cm/cm/°C |