TPE 6356-BKB09 DUPONT USA

Hytrel®

Toy,Luggage accessories,Medical devices

Aging resistance,Solvent resistant

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	DUPONT USA/6356-BKB09
Shore hardness	ShoreD	ISO 868	63
Shore hardness		ShoreD,15Sec	ISO 868	57

Supplementary Information	Test Condition	Test Method	DUPONT USA/6356-BKB09
EmissionofOrganicCompounds		VDA277	2.50 µgC/g
Odor		VDA270	2.50

thermal performance	Test Condition	Test Method	DUPONT USA/6356-BKB09
Brittle temperature		ISO 974	-96.0 °C
Glass transition temperature		ISO 11357-2	0.00 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	80.0 °C
Hot deformation temperature		1.8MPa,Unannealed	ISO 75-2/A	45.0 °C
Linear coefficient of thermal expansion	TD：23to55°C	ASTME831	1.7E-04 cm/cm/°C
		MD：--	ISO 11359-2	1.9E-04 cm/cm/°C
		TD：-40to23°C	ISO 11359-2	1.5E-04 cm/cm/°C
		MD：-40to23°C	ISO 11359-2	1.6E-04 cm/cm/°C
		TD：--	ISO 11359-2	1.8E-04 cm/cm/°C
		TD：EffectiveThermalDiffusivity	ISO 11359-2	5.44E-08 m²/s
Melting temperature		ISO 11357-3	210 °C
Vicat softening temperature	--	ISO 306/B50	100 °C
Vicat softening temperature		--	ISO 306/A50	195 °C

mechanical properties	Test Condition	Test Method	DUPONT USA/6356-BKB09
Bending modulus		ISO 178	290 Mpa
Nominal tensile fracture strain		ISO 527-2	500 %
Tensile creep modulus	1hr	ISO 899-1	248 Mpa
Tensile creep modulus		1000hr	ISO 899-1	182 Mpa
Tensile modulus		ISO 527-2	280 Mpa
Tensile strain	Yield	ISO 527-2	31 %
Tensile strain		Break	ISO 527-2	>300 %
tensile strength	5.0%Strain	ISO 527-2	12.0 Mpa
		10%Strain	ISO 527-2	15.0 Mpa
		100%Strain	ISO 527-2	19.0 Mpa
		Break	ISO 527-2	43.0 Mpa
		50%Strain	ISO 527-2	18.8 Mpa
		Yield	ISO 527-2	20.0 Mpa
Wear resistance		ISO 4649	110 mm³

Electrical performance	Test Condition	Test Method	DUPONT USA/6356-BKB09
Dielectric strength		IEC 60243-1	20 KV/mm
Dissipation factor	1MHz	IEC 60250	0.036
Dissipation factor		100Hz	IEC 60250	0.012
Relative permittivity	100Hz	IEC 60250	4.60
Relative permittivity		1MHz	IEC 60250	4.10
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	8E+13 ohms·cm

Physical properties	Test Condition	Test Method	DUPONT USA/6356-BKB09
density		ISO 1183	1.22 g/cm³
MediumDensity			1.06 g/cm³
melt mass-flow rate	230°C/2.16kg	ISO 1133	9.0 g/10min
Melt Volume Flow Rate (MVR)	230°C/2.16kg	ISO 1133	8.50 cm3/10min
Shrinkage rate	MD	ISO 294-4	1.5 %
Shrinkage rate		TD	ISO 294-4	1.5 %
SpecificHeatCapacity of Melt			2150 J/kg/°C
ThermalConductivityofMelt			0.15 W/m/K
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20 %
		23°C,24hr	ISO 62	0.50 %
		Saturation,23°C,2.00mm	ISO 62	0.60 %

impact performance	Test Condition	Test Method	DUPONT USA/6356-BKB09
Charpy Notched Impact Strength	23°C,Partial Break	ISO 179/1eA	120 kJ/m²
		-30°C	ISO 179/1eA	25 kJ/m²
		-40°C	ISO 179/1eA	15 kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	19 kJ/m²
		23°C	ISO 180/1A	81 kJ/m²
		23°C	ISO 8256/1	300 kJ/m²

flammability	Test Condition	Test Method	DUPONT USA/6356-BKB09
Extreme Oxygen Index		ISO 4589-2	21 %
FMVSS flammability		FMVSS302	SE
Fogging-G-value	condensate	ISO 6452	1E-04 g
UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	HB
		3.0mm	UL 94	HB
		1.5mm	IEC 60695-11-10,-20	HB
		1.5mm	UL 94	HB

elastomer	Test Condition	Test Method	DUPONT USA/6356-BKB09
tear strength	横向Flow	ISO 34-1	150 kN/m
tear strength		Flow	ISO 34-1	160 kN/m