Mechanical properties	Test Condition	Test Method	DUPONT USA/159
elongation at break	50mm/min，屈服	ISO 527-1/2	50%RH｜＞50 %
Impact strength of cantilever beam gap	-30℃	ISO 180/1A	50%RH｜4.3 kJ/m²
Tensile stress	屈服	ISO 527-1/2	50%RH｜52 Mpa
Charpy Notched Impact Strength	-30℃	ISO 179/1eA	50%RH｜4 kJ/m²
Impact strength of simply supported beam without notch	23℃	ISO 179/1eU	50%RH｜NB kJ/m²
Tensile modulus	1mm/min	ISO 527-1/2	50%RH｜1550 Mpa
Impact strength of cantilever beam gap	23℃	ISO 180/1A	50%RH｜6 kJ/m²
Impact strength of simply supported beam without notch	-30℃	ISO 179/1eU	50%RH｜NB kJ/m²
Charpy Notched Impact Strength	23℃	ISO 179/1eA	50%RH｜8 kJ/m²
Tensile strain	50mm/min，屈服	ISO 527-1/2	50%RH｜19 %

Electrical performance	Test Condition	Test Method	DUPONT USA/159
Linear coefficient of thermal expansion	流动	ASTM D-831	50%RH｜- 10-4/℃
dielectric temperature	0.45MPa	ISO 75-1/2	135 °C
Linear coefficient of thermal expansion	横向	ASTM E-831	50%RH｜- 10-4/℃
dielectric temperature	1.80MPa	ISO 75-1/2	50%RH｜- °C

Thermal performance	Test Condition	Test Method	DUPONT USA/159
vicat	20N	ISO 306	50%RH｜- °C
Melt Temperature	10℃/min	ISO 3146C	50%RH｜- °C