PA6 F234-C DSM Additive Manufacturing
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | DSM Additive Manufacturing/ F234-C |
|---|---|---|---|
| Puncture Resistance | 50.0µm | 内部方法 | 13.5 J/cm |
| Relative solution viscosity (RSV) | 甲酸 | 内部方法 | 3.40 |
| film | Test Condition | Test Method | DSM Additive Manufacturing/ F234-C |
|---|---|---|---|
| tensile strength | 50µm,CastFilm | ISO 527-3 | 83.0 MPa |
| OTr | 85%RH:23°C,50.0µm | DIS15105-1/-2 | 38 cm³/m²/bar/24hr |
| elongation | 断裂,50µm,铸造薄膜 | ISO 527-3 | 350 % |
| Tear strength of pants shape | 50µm,CastFilm，MD | ISO 6383-1 | 32.0 N/mm |
| Water Vapor Transmission Rate | 23°C,85%RH,50µm,铸造薄膜 | DIS15106-1/-3 | 35 g/m²/24hr |
| OTr | 0%RH:23°C,50.0µm | DIS15105-1/-2 | 26 cm³/m²/bar/24hr |
| film thickness | 50 µm | ||
| Tensile modulus | 50µm,铸造薄膜 | 内部方法 | 450 MPa |
| tensile strength | Yield,50µm,CastFilm | ISO 527-3 | 32.0 MPa |
| Mechanical properties | Test Condition | Test Method | DSM Additive Manufacturing/ F234-C |
|---|---|---|---|
| coefficient of friction | 与自身-静态,铸造薄膜 | ISO 8295 | 1.2 |
| 与自身-动态,铸造薄膜 | ISO 8295 | 1.0 |
| optical performance | Test Condition | Test Method | DSM Additive Manufacturing/ F234-C |
|---|---|---|---|
| transmissivity | 50.0µm,铸造薄膜 | 内部方法 | 83.0 % |
| physical property | Test Condition | Test Method | DSM Additive Manufacturing/ F234-C |
|---|---|---|---|
| viscosity number | ISO 307 | 229 cm³/g | |
| density | ISO 1183 | 1.13 g/cm³ | |
| melt viscosity | 260°C | 内部方法 | 1600 Pa·s |
| Thermal performance | Test Condition | Test Method | DSM Additive Manufacturing/ F234-C |
|---|---|---|---|
| Specific heat capacity | Average:20到150°C | 2250 J/kg/°C | |
| -- | 1550 J/kg/°C | ||
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9E-05 cm/cm/°C |