PBT 6300B JAPAN POLYPLASTIC
DURANEX®
Automotive Applications
Low warpage
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/6300B |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 90 |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/6300B |
|---|---|---|---|
| ColorNumber | EF2001/ED3002 |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6300B |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| Volume resistivity | IEC 60093 | 8E+15 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 20 KV/mm |
| Volume resistivity | ASTM D257/IEC 60093 | 8.0 x 10^15 Ω.cm | |
| IEC 60093 | 8×1015 Ω.cm | ||
| Surface Resistivity | IEC 60093 | 5×1016 Ω |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/6300B |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 91 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ISO 179/1eA | 2.0 kJ/m² | |
| Flexural modulus | ASTM D790/ISO 178 | 3900 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ISO 527-1/-2 | 53 Mpa | |
| bending strength | ISO 178 | 91.0 Mpa | |
| Flexural modulus | ISO 178 | 3900 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 5.0 % |
| 断裂 | ISO 527-1/-2 | 2.5 % | |
| elongation at break | ASTM D638/ISO 527 | 2.5 % | |
| tensile strength | ASTM D638/ISO 527 | 53 kg/cm²(MPa)[Lb/in²] | |
| ISO 527-2 | 55.0 Mpa |
| Physical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/6300B |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.53 |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/6300B |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/6300B |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.10 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6300B |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Linear coefficient of thermal expansion | 流动方向 | ISO 11359-2 | 9 ×10-5/℃ |
| TD：23to55°C | 内部方法 | 9E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8Mpa，HDT | ISO 75-1/-2 | 160 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | 内部方法 | 9E-05 cm/cm/°C |
| 垂直方向 | ISO 11359-2 | 9 ×10-5/℃ | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 110 °C |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 9 mm/mm.℃ | |
| UL flame retardant rating | UL 94 | HB |