PA6 B3M8 BASF GERMANY
Ultramid®
Electrical applications、Industrial machinery
Flame retardant、Oil resistant、Halogen-free
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/B3M8 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 120 kJ/m² |
| hardness | Test Condition | Test Method | BASF GERMANY/B3M8 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 119 |
| Supplementary Information | Test Condition | Test Method | BASF GERMANY/B3M8 |
|---|---|---|---|
| Dart impact | 23°C | 内部方法 | 6.78 J |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/B3M8 |
|---|---|---|---|
| bending strength | -40°C | ASTM D790 | 207 Mpa |
| Tensile modulus | 80°C | ISO 527-2 | 1360 Mpa |
| Flexural modulus | -40°C | ASTM D790 | 5860 Mpa |
| bending strength | 23°C | ASTM D790 | 138 Mpa |
| 65°C | ASTM D790 | 55.0 Mpa | |
| Tensile modulus | 23°C | ISO 527-2 | 6400 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 85.0 Mpa |
| 断裂,23°C | ASTM D638 | 90.0 Mpa | |
| Tensile modulus | -40°C | ISO 527-2 | 8310 Mpa |
| 150°C | ISO 527-2 | 910 Mpa | |
| bending strength | 90°C | ASTM D790 | 35.0 Mpa |
| Tensile modulus | 120°C | ISO 527-2 | 970 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 10 % |
| Flexural modulus | 90°C | ASTM D790 | 810 Mpa |
| bending strength | 121°C | ASTM D790 | 34.0 Mpa |
| Flexural modulus | 121°C | ASTM D790 | 815 Mpa |
| bending strength | 23°C | ISO 178 | 140 Mpa |
| Flexural modulus | 23°C | ISO 178 | 5200 Mpa |
| 65°C | ASTM D790 | 1540 Mpa | |
| 23°C | ASTM D790 | 5760 Mpa | |
| elongation | 断裂,23°C | ASTM D638 | 10 % |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/B3M8 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| 1.50mm | ASTM D257 | >1.0E+15 ohms·cm | |
| dielectric strength | 1.50mm | ASTM D149 | 22 KV/mm |
| physical property | Test Condition | Test Method | BASF GERMANY/B3M8 |
|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.90 % | |
| Water absorption rate | 饱和 | ASTM D570 | 5.7 % |
| 24hr | ASTM D570 | 1.1 % | |
| 23°C,24hr | ISO 62 | 1.1 % | |
| 平衡,50%RH | ASTM D570 | 1.6 % | |
| 平衡,23°C,50%RH | ISO 62 | 1.6 % | |
| 饱和,23°C | ISO 62 | 5.7 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/B3M8 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 195 °C |
| Linear coefficient of thermal expansion | MD | 4.6E-05 cm/cm/°C | |
| melting temperature | ASTM D3418 | 220 °C | |
| Linear coefficient of thermal expansion | MD | ASTME831 | 5E-05 cm/cm/°C |
| TD | 5.8E-05 cm/cm/°C | ||
| melting temperature | ISO 3146 | 220 °C |