PA6 1013G20 MITSUBISHI ENGINEERING JAPAN
Novamid®
Automotive sector、Electronic and Electrical
high strength、High rigidity、Fiber optic reinforcement
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1013G20 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 179 | 43(85) KJ/m | |
| Breaking stress | 150(90) Mpa | ||
| Tensile modulus | ISO 527-1 | 7300(4000) Mpa | |
| bending strength | D178 | 234(148) Mpa | |
| Flexural modulus | D178 | 6600(4200) Mpa | |
| elongation | 断裂 | 2.9(5.4) % |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1013G20 |
|---|---|---|---|
| dielectric strength | IEC 243-1 | 27 MV/m | |
| Dielectric loss | IEC 250 | 0.013(0.023) | |
| dielectric constant | D150 | 4 Pf/m | |
| Compared to the Leakage Traceability Index (CTI) | IEC 112 | 500 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1013G20 |
|---|---|---|---|
| Shrinkage rate | 0.3 MD% | ||
| 1.2 TD% | |||
| Water absorption rate | D570 | 2.8 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1013G20 |
|---|---|---|---|
| Heat distortion temperature | HDT | D648 | 199(217) °C |
| UL flame retardant rating | UL 94 | HB |