Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PSU S2010G6 BASF GERMANY
Ultrason®S
Food containers、Medical equipment、Printing machine parts、Electrical components
High temperature resistan、wear resistant、Filler: Glass fiber reinf、30% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/S2010G6 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 8.5 kJ/m² |
| -30°C | ISO 179 | 8.5 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 8.5 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 45 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180 | 8.5 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 40 kJ/m² |
| hardness | Test Condition | Test Method | BASF GERMANY/S2010G6 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 193 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/S2010G6 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 | |
| dielectric constant | 100Hz | IEC 60250 | 3.70 |
| dielectric strength | IEC 60243-1 | 45 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| dielectric constant | 1MHz | IEC 60250 | 3.70 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 6E-03 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/S2010G6 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.2 % |
| Tensile modulus | 23°C | ISO 527-2 | 8900 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 125 Mpa |
| flammability | Test Condition | Test Method | BASF GERMANY/S2010G6 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 1.6mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | BASF GERMANY/S2010G6 |
|---|---|---|---|
| Melt volume flow rate | 360°C/10.0kg | ISO 1133 | 30.0 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 0.46 % |
| MD | ISO 294-4 | 0.29 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.60 % | |
| density | ISO 1183 | 1.46 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/S2010G6 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | 2E-05 cm/cm/°C | |
| RTI Imp | 1.6mm | UL 746 | 140 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 185 °C |
| RTI Str | 1.6mm | UL 746 | 160 °C |
| 3.0mm | UL 746 | 160 °C | |
| RTI Elec | 1.6mm | UL 746 | 160 °C |
| 3.0mm | UL 746 | 160 °C | |
| RTI Imp | 3.0mm | UL 746 | 140 °C |