Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PS TOTAL Polystyrene Crystal 1960N 法国TOTAL石化
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Crystal 1960N |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 6.0 kJ/m² |
| hardness | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Crystal 1960N |
|---|---|---|---|
| Rockwell hardness | L计秤 | ISO 2039-2 | 70 |
| Mechanical properties | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Crystal 1960N |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3100 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 35.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| Flexural modulus | ISO 178 | 2900 MPa |
| Electrical performance | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Crystal 1960N |
|---|---|---|---|
| dielectric strength | 140 kV/mm | ||
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| physical property | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Crystal 1960N |
|---|---|---|---|
| Apparent density | 0.60 g/cm³ | ||
| Shrinkage rate | 0.40to0.70 % | ||
| melt mass-flow rate | 200°C/5.0kg | ISO 1133 | 30 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | <0.10 % |
| density | ISO 1183 | 1.05 g/cm³ |
| Thermal performance | Test Condition | Test Method | 法国TOTAL石化/TOTAL Polystyrene Crystal 1960N |
|---|---|---|---|
| Hot deformation temperature (HDT) | 1.8MPa,退火，HDT | ISO 75-2/A | 96.0 °C |
| vicat | 线形热膨胀系数-流动 | 7.1E-05 cm/cm/°C | |
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ISO 75-2/A | 84.0 °C |
| vicat | -- | ISO 306/A50 | 105 °C |
| -- | ISO 306/B50 | 101 °C |