Product Name

Brand Name

Usages

Properties

Certificates

PVDF 720 ARKEMA CHANGSHU

Kynar®

--

--

UL

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	ARKEMA CHANGSHU/720
Shore hardness	23℃	ASTM D2240	76-80

thermal performance	Test Condition	Test Method	ARKEMA CHANGSHU/720
decomposition temperature	TGA在通气中1%质量损失	内部测试方法	410 °C
decomposition temperature		TGA在空气中1 %质量损失	内部测试方法	375 °C
Glass transition temperature		ASTM D7028	-40.6-38.3 °C
Glass transition temperature		10℃/min	ISO 11357	-40 °C
Hot deformation temperature	0.45MPa120℃/hr	ASTM D648	125-140 °C
		1.8MPa	ISO 75	110 °C
		0.45MPa	ISO 75	132 °C
		1.8MPa120℃/hr	ASTM D648	105-115 °C
Linear coefficient of thermal expansion	Flow	ISO 11359	0.00015 m/m/k
Linear coefficient of thermal expansion		23℃	ASTM D696	1.19E-3 cm/cm/℃
Melting temperature		ASTM D3418	165-172 °C
Melting temperature		10℃/min	ISO 11357	168 °C
specific heat		内部测试方法	745-958 J/(kg.k)
thermal conductivity		ASTM E1461	0.17-0.19 W/(m.K)
Vicat softening temperature	50℃/hr 50N	ISO 306	139 °C

mechanical properties	Test Condition	Test Method	ARKEMA CHANGSHU/720
Bending modulus	23℃	ASTM D790	1380-2310 Mpa
bending strength	23℃5.0%Strain	ASTM D790	58.6-75.8 Mpa
Charpy Notched Impact Strength	-30℃	ISO 179	189 kJ/㎡
		-30°C	ISO 179	5 kJ/㎡
		23℃	ISO 179	208 kJ/㎡
Compression slip	23℃	ASTM D695	68.9-103 Mpa
elongation	Break	ISO 527	50 %
		Break23℃	ASTM D638	20-100 %
		Yield23℃	ASTM D638	570 %
		Yield	ISO 527	8 %
Friction coefficient	静态对钢23℃	ASTM D1894	0.14
Impact strength of cantilever beam gap	23℃	ASTM D256	0.0801-0.214 KJ/m
Suspended wall beam without notch impact strength	23℃	ASTM D256	1.07-4.27 KJ/m
Taber wear resistance	CS-17轮1kg	ASTM G195	5-9 mg/1000cy
Tensile modulus	23℃	ASTM D638	1380-2310 Mpa
Tensile modulus			ISO 527	2200 Mpa
tensile strength	Yield	ISO 527	54 Mpa
		Break23℃	ASTM D638	34.5-55.2 Mpa
		Yield23℃	ASTM D638	44.8-55.2 Mpa

flame retardant performance	Test Condition	Test Method	ARKEMA CHANGSHU/720
Extreme Oxygen Index		ISO 4589	43 %
Extreme Oxygen Index			ASTM D2863	44 %
UL flame retardant rating	1.5mm	UL 94	V-0

Electrical performance	Test Condition	Test Method	ARKEMA CHANGSHU/720
Accumulation resistor		IEC 60093	2000000000000 Ω.m
Compared to the anti leakage trace index		IEC 60112	PLC 0
Dielectric constant	iKHz	ASTM D150	4.5-9.5
		1MHz	IEC 60250	7
		100Hz	IEC 60250	9
Dielectric strength		IEC 60243	21 KV/mm
Dielectric strength		23℃	ASTM D149	1.7 KV/mm
Dissipation factor	1MHz	IEC 60250	0.214
		100Hz	IEC 60250	0.032
		100kHz	ASTM D150	0.01-0.21
Surface resistivity		IEC 60093	1000000000000000 Ω
Volume resistivity	20℃ 65RH	ASTM D257	200000000000000 Ω.cm

Physical properties	Test Condition	Test Method	ARKEMA CHANGSHU/720
density		ISO 1183	1780 kg/㎥
density		23℃	ASTM D792	1.77-1.79 g/㎤
melt mass-flow rate	230°C 3.8kg	ASTM D1238	5-26.5 g/10min
Melt viscosity	230℃100s	ASTM D3835	6-12 kPoise
Shrinkage rate	Flow	ISO 294	2 %
Shrinkage rate		垂直	ISO 294	2 %
Water absorption rate		ISO 62	0.015 %
Water absorption rate			ASTM D570	0.01-0.03 %
Yirong Index	230℃ 5kg	ISO 1133	10 ㎤/10min

UL	Test Condition	Test Method	ARKEMA CHANGSHU/720
Outdoor applicability		UL -746C	f1
RTI Elec	本色 1.5mm	UL 746B	150 °C
RTI Imp	本色 1.5mm	UL 746B	150 °C
RTI Str	本色 1.5mm	UL 746B	150 °C
UL flame retardant rating	1.5mm	UL 94	V-0

optical performance	Test Condition	Test Method	ARKEMA CHANGSHU/720
Refractive index	钠光谱D线	ASTM D542	1.42